1.
There are some measure condition intems which have influence on BH values of BH steel sheets during measure process, such as bake temperature, heating time and heating media, tensile speeds as well as different tensile machines.
BH值是超低碳BH钢板的一项特征值。
2.
BH values increase significantly,and the higher baking temperature has little effect on BH values.
结果发现在烘烤温度小于140℃时,BH值随着烘烤温度的增加而显著增加,烘烤温度高于140℃时,温度对其影响不大;2%预应变、140℃烘烤条件下,超低碳钢的烘烤硬化效应在数分钟内迅速表现出来,20分钟内达到最大,随保温时间的继续增加,BH值并无明显变化;预变形量对BH值有一定的影响,大于2%的预变形反而会减弱烘烤硬化效应。
4) BH hydrophobic agents
BH憎水剂
5) BH energizing reagent
BH催渗剂
1.
The results show that these carburized gears by using BH energizing reagent get finer microstructure,lower heat distortion,deeper carburizing layer,b.
实验结果表明使用BH催渗剂后的渗碳齿轮轮齿组织得到细化,热畸变减小,渗碳层深度增加,渗碳层碳化物分布形态得到改善,渗碳层硬度梯度趋于平缓。
6) ELC-BH steel plate
ELC-BH钢板
补充资料：bohrium Bh
分子式：
CAS号：
性质：人工合成的锕系后元素。1976年苏联Dubna联合核子所的G. N. Flerov和Y. T. Oganessian等人用54Cr轰击209Bi靶，通过核反应：209Bi(54Cr,2n)261Bh，得到了261Bh，但国际理论和应用化学联合会与国际理论和应用物理学联合会认为以上工作还缺乏充分证据；1981年联邦德国Darmstadt重离子研究所的G. Munzenberg和P. Armbruster等人在“全粒子加速器”上用54Cr轰击209Bi靶观察得到262Bh，1986年，他们又合成了其同位素，其中262Bh的半衰期为102ms±26ms。
CAS号：
性质：人工合成的锕系后元素。1976年苏联Dubna联合核子所的G. N. Flerov和Y. T. Oganessian等人用54Cr轰击209Bi靶，通过核反应：209Bi(54Cr,2n)261Bh，得到了261Bh，但国际理论和应用化学联合会与国际理论和应用物理学联合会认为以上工作还缺乏充分证据；1981年联邦德国Darmstadt重离子研究所的G. Munzenberg和P. Armbruster等人在“全粒子加速器”上用54Cr轰击209Bi靶观察得到262Bh，1986年，他们又合成了其同位素，其中262Bh的半衰期为102ms±26ms。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条