1) erosion-oxidation
冲蚀-氧化
1.
In this paper,the methods have been found out to improve the resistance for the high temperature erosion-oxidation of plastic dies through the research for the reason of erosion-oxidation of dies surface that causes the invalidation of dies.
通过对塑料模使用过程中表面高温冲蚀-氧化机理的研究,得出造成模具尺寸精度下降和表面粗糙度值提高的原因,提出提高塑料模具抗高温冲蚀-氧化现象的措施。
2) high temperature oxidation and erosion
高温氧化与冲蚀
3) oxidative corrosion
氧化腐蚀
1.
By expounding oxidative corrosion of the lead-acid battery,nonreversible sulfation of the polar plate,expansion drop of the negative plate active matter,local anti-polar.
通过对铅酸蓄电池正极柱氧化腐蚀、极板的不可逆硫酸盐化、负极板活性物质的膨胀脱落、极板的局部反极等现象的阐述 ,分析和解释造成电瓶损坏的主要原因 ,同时提出改进措施。
4) Oxidation Corrosion
氧化腐蚀
1.
In addition,the oxidation corrosion was reduced under oxygen deprived condition as a result of the presence of the grease around the contact interface and the separated oil at the contact interface.
同时,接触界面周围的脂和磨坑表面的油减少了空气与摩擦表面的接触,使接触界面氧化腐蚀得以降低;磨坑表面高硬度白层因稳态低摩擦力而持续存在,有益于减缓微动磨损。
5) oxidation and erosion
氧化腐蚀
1.
The results show that working for long time under high temperature,the wall of reheater pipe is severely thinned with action of oxidation and erosion on the inside and outside surface,and the material of pipe becomes brittle and the intergranular crack forms.
结果表明,由于长时高温运行,再热器管在内外表面氧化腐蚀作用下,管壁严重减薄,材料组织脆化,形成沿晶裂纹,管子不足以承受管内蒸汽压力,形成脆性开裂爆口。
补充资料：冲蚀
冲蚀
erosion corrosion
ehongsh-冲蚀(erosion corrosion)金属材料表面与腐蚀流体冲刷的联合作用，而引起材料局部的金属腐性。在发生这种腐蚀时，金属离子或腐蚀产物因受高速腐蚀流体冲刷而离开金属材料表面，使新鲜的金属表面与腐蚀流体直接接触，从而加速了腐蚀过程。若流体中悬浮较硬的固体颗粒，则将加速材料的损坏。一般说来，流体的速度愈高，流体中悬浮的固体颗粒愈多、愈硬，冲刷腐蚀速度愈快。腐蚀介质流动速度又取决于流动方式:层流时，由于流体的粘度，在沿管道截面有一种稳态的速度分布;湍流时，破坏了这种稳态速度分布，这不仅加速了腐蚀剂的供应和腐蚀产物的迁移，而且在流体与金属之间产生切应力，能剥离腐蚀产物，从而加大了冲蚀速度。因此，在管道的拐弯处及流体进入管道或贮罐处容易产生这种破坏。另外，金属表面成膜的特征也可以影响冲蚀速度。硬的、致密的、连续的、粘附性强的膜冲蚀速度小，反之则大。抑制或减少冲蚀的措施是:选择耐蚀性和耐磨性好的材料;改变腐蚀环境如添加缓蚀剂，过滤悬浮固体粒子，降低温度，减小流速和湍流;采用栖牲阳极作阴机保护等。 (1陈树俊l)