1) 3D woven thermoplastic composites
三维机织热塑性复合材料
1.
In order to solve the two d ifficult problems of 3D woven preform weaving in 3D woven thermoplastic composites and resin impregnating of 3D preforms, the new technique for preparing 3D woven thermoplastic compos- ites is developed, with the process ofm icro-braided yarn knitting, i.
为了解决三维机织热塑性复合材料中三维机织预型件的织造和热塑性基体浸入预型件这两大难题,开发了制备三维机织热塑性复合材料的新工艺,即微编纱的编织-用微编纱织造三维机织预型件-复合固化成型。
2) 3D woven composites
三维机织复合材料
1.
A multiple scale viscoelastic model for the 3D woven composites was suggested.
建立了一种三维机织复合材料多尺度的黏弹性分析模型。
2.
Based on observing and analyzing digital images and microstructure of 3D woven composites cross-sections,the results show that the position of deciding the thickness of 3D woven composites is located at the cross-section which passes through the center of the weft thread,the cross-section of a warp thread is rectangular,and the longitudi.
对三维机织复合材料横截面图像细观结构进行观察分析。
3.
Therefore,it\'s a great trend to study and develop conformal load-bearing microstrip antennas based on 3D woven composites for next generation.
然而,复合材料层合板在结构上具有抗层间分离能力差、制作方法复杂、结构不规整无法制造全成形天线结构等缺点,因此大力发展基于三维机织复合材料的共形承载微带天线是研发下一代共形承载天线的必然趋势。
3) D woven composites
三维机织复合材料
1.
A combined beam model representing the periodicity of the microstructure and micro deformation of 3D woven composites is developed for predicting mechanical properties.
根据三维机织复合材料中细观几何和变形的周期性 ,提出了一种反映细观周期约束条件的组合梁单元模型 ,该模型既考虑了纤维束的偏轴拉压效应 ,又考虑了纤维束的弯 /剪耦合效应和纤维束之间的相互作用 ,可以描述纤维束和基体中的细观应力分布。
2.
The micro-geometry-structure of a 3D woven composites is studied.
对三维机织复合材料的细观几何结构进行了深入的研究。
4) 3-D orthogonal woven composite
三维正交机织复合材料
1.
As for 3-D orthogonal woven composite,a new homogenized eigen-element method is proposed in this paper.
基于三维正交机织复合材料,提出了一种特征单元均匀化分析方法。
2.
As a typical 3-D construction composite, 3-D orthogonal woven composites is famous for its excellent mechanical property, especially the high resistance of delaminate and fracture.
三维正交机织复合材料是一种典型的三维纺织结构复合材料，由于Z方向绑定纱的引入，使其在各种三维结构复合材料中脱颖而出，尤其是抗冲击性能极其优秀，在高性能复合材料领域中得到首肯。
5) 3-D cellular woven composite
三维多胞机织复合材料
1.
3-D cellular woven composites have widely applications to aircrafts, vehicles, ships and sports facilities because of the high ratio of strength/weight and high energy absorption under impact loading.
该论文旨在表征三维多胞机织复合材料的细观结构、冲击响应和在冲击加载下破坏特征。
6) Thermoplastic Composite
热塑性复合材料
1.
Research on properties of flax and low melt point PET thermoplastic composites;
亚麻/低熔点聚酯纤维热塑性复合材料性能研究
2.
Review of thermoplastic composites from commingled yarns;
混纤纱制备热塑性复合材料研究评述
3.
Evaluation of mechanical properties of thermoplastic composites based on flax/polypropylene core-spun yarns
亚麻/丙纶包覆纱热塑性复合材料力学性能的评判(英文)
补充资料：热塑性树脂基复合材料
分子式：
CAS号：
性质：以热塑性树脂为基体，以填料填充或以纤维（或其织物）增强的复合材料。原则上所有的热塑性塑料都可用作复合材料的基体，常用的有聚丙烯（等规）、聚酰胺（即尼龙），饱和聚酯（如聚对苯二甲酸乙二酯、聚对苯二甲酸丁二酯）、聚碳酸酯、聚苯硫醚、聚醚酮、热塑性聚酰亚胺、聚苯醚、聚砜、聚四氟乙烯、聚氯乙烯、聚苯乙烯和液晶高聚物等。常用的增强纤维是玻璃纤维、碳纤维、芳纶；常用的填料有碳酸钙、云母、石墨、滑石粉、二硫化钼；也可用金属粉。与热固性树脂基复合材料相比，热塑性树脂基复合材料具有韧性高、成型工艺简单、吸湿性小、容易修补、可作二次成型、预浸料在室温下可无限期贮存等优点。在损伤容限或降低成本方面具有优势。目前热塑性树脂基长时复合材料尚存在的主要问题是：成型中需同高温高压；高黏度熔体浸润纤维比较困难；有可能出现环境应力开裂。
CAS号：
性质：以热塑性树脂为基体，以填料填充或以纤维（或其织物）增强的复合材料。原则上所有的热塑性塑料都可用作复合材料的基体，常用的有聚丙烯（等规）、聚酰胺（即尼龙），饱和聚酯（如聚对苯二甲酸乙二酯、聚对苯二甲酸丁二酯）、聚碳酸酯、聚苯硫醚、聚醚酮、热塑性聚酰亚胺、聚苯醚、聚砜、聚四氟乙烯、聚氯乙烯、聚苯乙烯和液晶高聚物等。常用的增强纤维是玻璃纤维、碳纤维、芳纶；常用的填料有碳酸钙、云母、石墨、滑石粉、二硫化钼；也可用金属粉。与热固性树脂基复合材料相比，热塑性树脂基复合材料具有韧性高、成型工艺简单、吸湿性小、容易修补、可作二次成型、预浸料在室温下可无限期贮存等优点。在损伤容限或降低成本方面具有优势。目前热塑性树脂基长时复合材料尚存在的主要问题是：成型中需同高温高压；高黏度熔体浸润纤维比较困难；有可能出现环境应力开裂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条