1) double crucible Czochralski method
双坩埚提拉法
1.
The direct experimental data of constitutional supercooling during the crystal growth of near-stoichiometric lithium niobate by double crucible Czochralski method were observed and the theoretical issues of the critical growth rate were treated based on the stability criterion equation.
本文在用双坩埚提拉法生长近化学计量比LiNbO3晶体的过程中观察到了组分过冷的实验数据,同时根据Tiller-Chalmers稳定性判据公式半定量计算了近化学计量比LiNbO3晶体临界生长速率的理值,得到一般电阻加热双坩埚提拉法生长近化学计量比LiNbO3晶体的临界生长速率为0。
2.
Phenomena of mechanical twinning, constitutional supercooling, inclusions of the stoichiometric LiNbO_3 crystal grown by double crucible Czochralski method were observed and analyzed in this paper.
本文对采用双坩埚提拉法(DCCZ)生长的化学计量比LiNbO3晶体中出现的机械双晶、组分过冷、包裹体等宏观生长缺陷进行了观察和分析。
2) Double-crucible method
双坩埚法
3) marble nelt process,crucible method,remelt process
坩埚法拉丝
4) remelt process
坩埚拉丝法
5) double crucible method
双坩埚方法
6) double crucible method
双重坩埚法
补充资料：提拉法
分子式：
CAS号：
性质：一种生长单晶的常用方法。将生长晶体用的材料置于适当的坩埚中加热熔融，使熔体保持在略高于材料熔点的温度下。将固定在拉杆上的籽晶与熔体表面接触，拉杆在不停地旋转中缓缓地向上提升。拉杆的散热作用使子晶上产生一定的温度梯度，促使熔体在晶体的下端不断地结晶。这种方法可以直接观测到晶体的生长过程，并可以通过调整各种条件得到大尺寸的单晶体。很多重要的无机固体材料的单晶体都可以利用这种方法制造，特别适合于生产大尺寸的技术晶体。
CAS号：
性质：一种生长单晶的常用方法。将生长晶体用的材料置于适当的坩埚中加热熔融，使熔体保持在略高于材料熔点的温度下。将固定在拉杆上的籽晶与熔体表面接触，拉杆在不停地旋转中缓缓地向上提升。拉杆的散热作用使子晶上产生一定的温度梯度，促使熔体在晶体的下端不断地结晶。这种方法可以直接观测到晶体的生长过程，并可以通过调整各种条件得到大尺寸的单晶体。很多重要的无机固体材料的单晶体都可以利用这种方法制造，特别适合于生产大尺寸的技术晶体。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。