1) chemical degreasing
化学脱脂
1.
It mainly introduces the chemical degreasing method for electrical steel, the material used in degreasing process, the factor of influencing the degreasing process, as well as the treatment of familiar problems during degreasing etc.
介绍了电工钢化学脱脂方法、脱脂所用的材料、影响脱脂工艺的因素以及脱脂常见问题及处理。
2) electrochemical degreasing
电化学脱脂
3) solvent extraction debinding
化学溶剂脱脂
4) catalytic debinding
催化脱脂
1.
Study on the catalytic debinding type binder for MIM;
注射成形用催化脱脂型粘结剂的研究
2.
In this paper,a new technology known as catalytic debinding was adopted at a temperature lower than the melt temperature of hte main binder,and the whole process could be finished in ten hours or so.
本研究采用以聚甲醛为主要粘结剂制备了可快速脱脂的新型陶瓷注射成形喂料体系 ,并进行催化脱脂工艺的研究 ,记录了该过程中样品失重的情况 ,分析了脱脂阶段不同特征及其原因 ,指出催化脱脂过程速度的控制因素是气态催化剂和气体产物扩散过程。
3.
The mechanisms of catalytic debinding and aqueous extraction debinding are discussed in detail.
脱脂是陶瓷注射成型中最复杂、最重要的环节 ,本文介绍了陶瓷注射成型最新脱脂工艺进展 ,详细介绍了催化脱脂和水基萃取脱脂的脱脂原理 ,并对各种脱脂工艺的优缺点进行了比较。
6) kinetics of debinding
脱脂动力学
补充资料：化学脱脂
分子式：
CAS号：
性质：通过碱或碱性溶液、表面活性剂的皂化和乳化作用清除电镀零件表面的油脂的过程。钢铁零件脱脂，碱溶液中含氢氧化钠量应小于100g·L-1。对铜及其合金件其量应小于20g·L-1，而锌、锡、铅、铝及其合金件，最好使用碳酸钠、磷酸钠等溶液。碱溶液能与动、植物油起皂化反应。加入少量乳化剂如硅酸钠、皂粉、OP乳化剂、洗涤剂等可以除去矿物油，脱脂液的温度一般为70～100℃。经脱脂后的零件一定要清洗干净，否则会影响镀层结合力。
CAS号：
性质：通过碱或碱性溶液、表面活性剂的皂化和乳化作用清除电镀零件表面的油脂的过程。钢铁零件脱脂，碱溶液中含氢氧化钠量应小于100g·L-1。对铜及其合金件其量应小于20g·L-1，而锌、锡、铅、铝及其合金件，最好使用碳酸钠、磷酸钠等溶液。碱溶液能与动、植物油起皂化反应。加入少量乳化剂如硅酸钠、皂粉、OP乳化剂、洗涤剂等可以除去矿物油，脱脂液的温度一般为70～100℃。经脱脂后的零件一定要清洗干净，否则会影响镀层结合力。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。