1) molding temperature
成型温度
1.
Analysis on the influences of various molding temperatures on performance of AC-13 mixture;
不同成型温度对AC-13混合料性能影响分析
2.
Influences of plasticizing temperature and molding temperature on mechanical properties of plasticized PVC and PVC/PNBR elastomer
塑化温度和成型温度对增塑PVC及PVC/PNBR弹性体力学性能的影响
3.
During the process of the consolidation molding consolidation, this paper adopts three schemes to make kinds of samples, while it gives and studies the molding temperature as well as adopts the molding pressure, analyzing the relationship between the molding pressure and the molding thickness.
模塑成型的复合固化中,采用了三个方案复合出几种试样,并对试样的成型温度,成型压力的确定给予了探讨,同时分析了成型压力与成型厚度之间的关系。
2) forming temperature
(热)成型温度
3) Temperature regime of compressing
成型温度制度
4) injection-molding temperature
注射成型温度
5) forming range
(热)成型温度范围
6) plug temperature
模塞温度(热成型)
补充资料：注塑成型之模具温度
在模具设计及成型工程的条件设定上，重要的是不仅维 持适合的温度，还要能让其均匀分布。不均匀的模温分布，会导致不均一的收缩和内应力，因而使成形品易产生变形和翘曲。
模温的高低会影响塑料在模腔内硬化的速度，太低会 使充填较困难以及未适当的收缩(或再结晶)即硬化，使得成型品有较多的充填和热应力之残留；太高则容易出现毛边及需要较长的冷却时间。
提高模温可以获致以下的效果：
1.增加成形品结晶度及较均匀的结构。
2.使成形收缩较充分，后收缩减少。
3.提高成形品的强度和耐热性。
4.减少内应力残留、分子配向及变形。
5.减少充填时的流动阻抗，降低压力损失。
6.使成形品外观光泽较低。
7.增加成形品发生毛边的机会。
8.增加近浇口部位和减少远浇口部位凹陷的机会。
9.减少结合线明显的程度。
10.增加冷却的时间。
模温的高低会影响塑料在模腔内硬化的速度，太低会 使充填较困难以及未适当的收缩(或再结晶)即硬化，使得成型品有较多的充填和热应力之残留；太高则容易出现毛边及需要较长的冷却时间。
提高模温可以获致以下的效果：
1.增加成形品结晶度及较均匀的结构。
2.使成形收缩较充分，后收缩减少。
3.提高成形品的强度和耐热性。
4.减少内应力残留、分子配向及变形。
5.减少充填时的流动阻抗，降低压力损失。
6.使成形品外观光泽较低。
7.增加成形品发生毛边的机会。
8.增加近浇口部位和减少远浇口部位凹陷的机会。
9.减少结合线明显的程度。
10.增加冷却的时间。