1) Micro-indentation hardness
微压入压痕
2) micro-indentation
微压痕
1.
modulus of elasticity and creep strain rate sensitivity by using depth-sensing micro-indentation with the influence of loading rates on load—displacement (Fh) relationship.
介绍了一种测量其力学性能的新方法,即通过微压痕仪精确测量不同加载速率下压子的压入深度h与加载载荷F的关系来确定钎料的弹性模量E和蠕变速率敏感指数m。
2.
Investigations of the plasticity,damage and fracture induced by micro-indentation are reviewed.
主要结果:微压痕诱导硅和砷化镓晶体的纳米和非晶转变,并发现这一转变的临界应力;转变过程是由切应力,并非静水压力控制;电子辐照诱导非晶晶化,并发现晶化临界条件;晶化速率与电流密度有关;压痕诱发的裂纹尖端不是原子尖的,其萌生与扩展伴随位错的产生,并由此引发点阵的畸变,并产生1～2nm宽非晶带;裂纹扩展沿非晶带发生,而非裂端前方原子键相继断裂的结果;经傅立叶变换和逆变换发现,裂纹尖端变形显示出各向异性。
3) micro-indentation
显微压痕
1.
TEM observations of the dislocations from micro-indentation surface in single crystalline silicon at room temperature;
室温下单晶硅显微压痕表面位错组态的TEM观察
4) micro/nano indentation
微纳米压痕
5) interfacial frictional shear strength
亚微压痕仪
1.
The indentation method for measuring the interfacial frictional shear strength in a series of metal matrix composites(MMC)is presented.
用自制的亚微压痕仪测得了一组金属基复合材料的载荷－位移曲线，以决定纤维从基体中拔出时的滑动力。
6) microhardness method
显微硬度压痕法
补充资料：压痕
压痕
rolled pit
yahen压痕(r olled pit)钢材表面缺陷之一，系产品表面上被外物压成的局部凹坑，呈周期性单个或多个断续分布。一般产品表面允许有深度不超过标准规定的压痕。 产生原因是:(1)周期性压痕是由于成品孔或成品前孔、矫直辊、出口辊动导板(见导板)、导辊等粘有凸起物;(2)异物掉在轧件上，经轧后脱落;(3)产品在运送、保管过程中与硬物碰压或产品本身相互格压。 防止和消除办法有:(l)生产中定期检查轧件、轧糟、矫直辊和辊动导板，发现问题及时处理;(2)轧制时防止异物掉在轧件上;(3)吊运产品要平稳，产品包装要平齐，捆扎要牢固，堆放底脚要垫平。 (刘肾才)