1) D2 die steel for cold working
D2冷作模具钢
2) cold-working die steel
冷作模具钢
1.
Optimization design of the heat treatment process for high-carbon and high-alloy cold-working die steel;
高碳高合金冷作模具钢热处理工艺优化设计
2.
The effects of heat treatment process on the microstructure and properties of castinghigh-alloy cold-working die steel were discussed.
讨论了热处理工艺对铸造新型高合金冷作模具钢组织与性能的影响,结果表明,采用循环球化退火及1110℃淬火520℃两次回火得到的性能最佳,回火组织为回火马氏体及残余奥氏体,其硬度可达57～60HRC,冲击韧度8～10J/cm2。
3.
A cold-working die steel DM9 was developed by means of phase equilibrium thermodynamic calculation and the regime of different carbides with temperature.
应用相平衡热力学计算和根据碳化物随温度变化规律 ,研制的冷作模具钢DM9,因存在多类型碳化物 (M6 C ,M3C ,M2 3C6 、M7C3和MC) ,在常规的锻轧加工和退火工艺条件下 ,碳化物颗粒具有超细化特征。
3) cold-work die steel
冷作模具钢
1.
Study on strengthening and toughening of cold-work die steel XW-42;
冷作模具钢XW-42强韧化工艺研究
4) cold working die steels
冷作模具钢
1.
Properties and types of cold working die steel were summarized,and the disadvantages of traditional cold working die steels and advantages of new cold working die steels were put forward.
综述了冷作模具钢的性能及分类,指出了传统冷作模具钢的局限性和新型冷作模具钢的优势。
2.
Compared with the mechanical properties and the treatment processes of the cold working die steels,the three types of failure for the die steels,which are overload failure,wear failure and fatigue failure were analyzed.
通过对比几种典型冷作模具钢的处理工艺及其力学性能,综合分析了该类模具钢失效的3种类型,即过载失效、磨损失效和疲劳失效的形态和特征;重点探讨了高硬度冷作模具钢的表面开裂敏感性、缺口断裂性能和断口分形维数与工艺参数的关系,提出一些提高冷作模具断裂抗力、减少模具早期失效的途径。
5) cold working die steel
冷作模具钢
1.
Development and Application of High Toughness Cold Working Die Steel(DS Steel);
高韧性冷作模具钢(DS钢)的研究及应用
2.
Wear Resistance of Electroless Ni-P-SiO_2 Composite Deposits for Cold Working Die Steel;
冷作模具钢化学镀Ni-P-SiO_2复合镀层的耐磨性
3.
The cold working die steel with high-carbon and high-chromium are widely used due to its high hardness and good wear resistance.
高碳高铬冷作模具钢由于具有较高的硬度和良好的耐磨性而被广泛使用,但此类钢在凝固过程中,由于合金元素的偏析,会形成大量粗大的沿晶界连续分布的网状共晶碳化物,它的存在使钢的强度和韧性明显降低,严重缩短了模具使用寿命。
6) cold die steel
冷作模具钢
1.
A new developed less or non ledebrite high alloy tool steel less or non ledebrite high speed steel and less or non ledebrite high alloy cold die steel and their heat treatments were recommended in this paper.
全面介绍了新发展的少无莱氏体高合金工具钢 (少无莱氏体高速钢及少无莱氏体高合金冷作模具钢 )及其热处
2.
The experimental results will perfect the mechanism of the secondary hardening of cold die steel D2.
研究了D2冷作模具钢淬火后,在不同温度下回火的组织及性能变化规律,结果表明,引起D2钢二次硬化的原因,除了残留奥氏体的转变以外,另一个重要因素是VC,Mo_2C 等强化相的析出和沉淀。
补充资料：冷作模具钢
分子式：
CAS号：
性质：制造在冷状态下使金属变形的模具用的工具钢，也称做冷变形模具钢或冷模钢。冷作模具钢应该具有高的硬度和耐磨性、高的强度和疲劳强度以及足够的韧性，还要有良好的工艺性能，如锻造性、切削加工性、淬透性、淬硬性，且热处理变形小。典型的冷作模具钢有：(1)碳素工具钢T8～T12；(2)9Mn2V、9CrSi、MnSi、CrWMn等；(3)高韧性的4CrW2Si、5CrW2Si、6Cr2Si等；(4)高淬透性、高耐磨性和淬火变形小的Cr12、Cr12V、Cr12MoV、Cr6WV、Cr4W2MoV和CrMn2SiWMoV等。
CAS号：
性质：制造在冷状态下使金属变形的模具用的工具钢，也称做冷变形模具钢或冷模钢。冷作模具钢应该具有高的硬度和耐磨性、高的强度和疲劳强度以及足够的韧性，还要有良好的工艺性能，如锻造性、切削加工性、淬透性、淬硬性，且热处理变形小。典型的冷作模具钢有：(1)碳素工具钢T8～T12；(2)9Mn2V、9CrSi、MnSi、CrWMn等；(3)高韧性的4CrW2Si、5CrW2Si、6Cr2Si等；(4)高淬透性、高耐磨性和淬火变形小的Cr12、Cr12V、Cr12MoV、Cr6WV、Cr4W2MoV和CrMn2SiWMoV等。