1) PMnN-PZT
铌锰锆钛酸铅
1.
Sintering Behavior of PMnN-PZT Ceramics;
铌锰锆钛酸铅压电陶瓷烧结行为的研究
2) PMMN
铌镁-铌锰-锆钛酸铅
1.
PMMN-quaternary system piezoelectric ceramics with excess amounts of MgO were prepared by solid sintering method.
采用固相烧结法制备添加过量MgO的铌镁-铌锰-锆钛酸铅(PMMN)四元系压电陶瓷材料,研究了不同MgO掺杂量对材料结构及压电介电性能的影响。
3) PZN-PSN-PMS-PZT
铌锌-铌锡-锑锰-锆钛酸铅
4) lead niobium manganese zirconate titanate powder
铌锰锆钛酸铅系粉体
5) PMN-PMS-PZT
铌锰酸铅-锑锰酸铅-锆钛酸铅(PMN-PMS-PZT)
1.
The PMN-PMS-PZT ceramics was prepared by the solid-state,cold isostatic pressing and Gelcasting method respectively and a contrasted study of these preparing methods were carried out.
采用干压、冷等静压和凝胶注模等不同成型工艺制备铌锰酸铅-锑锰酸铅-锆钛酸铅(PMN-PMS-PZT)陶瓷,并进行对比研究。
6) lead manganese antimony-lead zinc niobate-lead zirconate titanate ceramics
锰锑酸铅-锌铌酸铅-锆钛酸铅陶瓷
补充资料：锑锰-锆钛酸铅压电陶瓷
分子式：Pb(Mnl/3Sbl/3)xTiZrzO3，x+y+z=l
CAS号：
性质：复合钛钙矿结构三元系压电陶瓷。具有机电耦合系数高(Kp 0.65~0.70)、机械品质因数好(Qm≥2000)、介质损耗小(tgδ≤40×10-4)、介质常数大和稳定性好等优点。主要原料为四氧化三铅、二氧化钛、二氧化锆、二氧化锰(或碳酸锰)、三氧化二锑，掺入少量改性氧化物，经700～850℃预烧、1100～1300℃烧结制成。通过调整式中x、y和z的比例，可在较宽范围内调整机电耦合系数(0.2～0.70左右)。可用于制造压电陶瓷滤波器、变压器、换能器等。
CAS号：
性质：复合钛钙矿结构三元系压电陶瓷。具有机电耦合系数高(Kp 0.65~0.70)、机械品质因数好(Qm≥2000)、介质损耗小(tgδ≤40×10-4)、介质常数大和稳定性好等优点。主要原料为四氧化三铅、二氧化钛、二氧化锆、二氧化锰(或碳酸锰)、三氧化二锑，掺入少量改性氧化物，经700～850℃预烧、1100～1300℃烧结制成。通过调整式中x、y和z的比例，可在较宽范围内调整机电耦合系数(0.2～0.70左右)。可用于制造压电陶瓷滤波器、变压器、换能器等。