The results show that the longitudinal flexural strength increases while the transverse compressive strength decreases with increasing the number of fabric layer at certain extent; The effects of angle of fabric layer on longitudinal flexural strength and transverse compressive strength are also different.
研究表明:随着织物铺层层数在一定范围内的增多,织物增强水泥基复合材料的纵向抗折强度逐渐增大,而横向抗压强度却逐渐下降;织物铺层角度对织物增强水泥基复合材料纵向抗折强度和横向抗压强度有不同影响,在所试验的范围内,纵向抗折强度以45°织物铺层角度为最好,0°的次之,90°的最差,而横向抗压强度却以0°织物铺层角度为最好,90°的次之,45°的最差;织物铺层位置对织物增强水泥基复合材料纵向抗折强度和横向抗压强度的影响在不同的情况下有较大的差别。
2) angle of layer
铺层角度
1.
ince changing the angle of layer of performs will have an effect on the mechanical property of the composite,flax fiber was used as the reinforcing material in preparing the prefabricated material with polylactic acid fiber which had been subjected to opening,blending and carding.
针对预成型件的铺层角度对复合材料力学性能产生影响的问题,以亚麻纤维为增强体,与聚乳酸纤维通过开松、混合、梳理工序制成预成型件后,采用模压成型工艺制备了亚麻纤维/聚乳酸复合材料。
3) number of fabric layer
织物铺层层数
1.
The results show that the longitudinal flexural strength increases while the transverse compressive strength decreases with increasing the number of fabric layer at certain extent; The effects of angle of fabric layer on longitudinal flexural strength and transverse compressive strength are also different.
研究表明:随着织物铺层层数在一定范围内的增多,织物增强水泥基复合材料的纵向抗折强度逐渐增大,而横向抗压强度却逐渐下降;织物铺层角度对织物增强水泥基复合材料纵向抗折强度和横向抗压强度有不同影响,在所试验的范围内,纵向抗折强度以45°织物铺层角度为最好,0°的次之,90°的最差,而横向抗压强度却以0°织物铺层角度为最好,90°的次之,45°的最差;织物铺层位置对织物增强水泥基复合材料纵向抗折强度和横向抗压强度的影响在不同的情况下有较大的差别。
4) position of fabric layer
织物铺层位置
5) the formation of fabric layers
织物铺层形式
6) ply angles
铺层角
1.
Sensitivity of the eigenvalues to the ply angles for composite plate;
层合板振动特征值对铺层角的灵敏度
补充资料：铺层器
分子式：
CAS号：
性质：又称铺层器。在平板支持物上，将固定相及黏合剂制成的浆状物均匀地涂布成薄层，制成薄层板的装置。薄层涂布器大致可分为固定式涂布器和移动式涂布器。有手工操作的，也有自动涂布装置。
CAS号：
性质：又称铺层器。在平板支持物上，将固定相及黏合剂制成的浆状物均匀地涂布成薄层，制成薄层板的装置。薄层涂布器大致可分为固定式涂布器和移动式涂布器。有手工操作的，也有自动涂布装置。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条