1) Germanium vitalization rate
锗挥发率
2) volatilizing rate
挥发率
1.
The experiment results indicate that zinc volatilizing rate is greater than 95%,lead volatilizing rate than 97%,under the conditions of coal rations 50% of slag mass,reduci.
85倍的条件下,锌的挥发率高于95%,铅的挥发率高于97%。
3) volatility
[英][,vɔlə'tiliti] [美][,vɑlə'tɪlətɪ]
挥发率
1.
The secondorder function of volatility of mould powder base (CaF_2CaOSiO_2Na_2O) with basicity, Na_2CO_3, CaF_2, temperature and time has been established through orthogonal design.
通过回归正交设计确定了连铸保护渣基料（ＣａＦ２－ＣａＯ－ＳｉＯ２－Ｎａ２Ｏ）挥发率与碱度、Ｎａ２ＣＯ３、ＣａＦ２含量、温度及时间的二次函数关系式。
2.
When the modified basicity of the slag R ′>1 and contents remain constant, volatility is raised greatly only when temperature exceeds the flow temperature; when temperature remains constant, volatility increases with basicity and Na 2CO 3; when R ′<1.
采用失重法对ＣａＯ－ＳｉＯ２－Ｎａ２Ｏ三元渣系在不同温度下的挥发率进行了测量。
3.
The relationship of the volatility of Ternary Flux CaO SiO 2 CaF 2 to temperature and the slag composition was studied using losing mass method.
通过质量损失法对ＣａＯ－ＳｉＯ２－ＣａＦ２三元渣系挥发率与温度、渣组成的关系进行了研究。
4) Volatilization rate
挥发速率
1.
The volatilization rate constants increase with increasing pH and temperature in water,and are larger in high wind speed above water surface than in tower wind speed.
水中氨氮挥发速率常数随水的pH值和水温升高而增加,水面风速大则常数值也大,大气压高的地区的挥发速率常数小于大气压低者。
2.
A good positive correlation between the gas-seawater partition coefficients and the measured volatilization rates of OCPs is observed.
结果表明,低浓度SDBS的存在能抑制OCPs的挥发,抑制能力有随SDBS浓度增加而增加的趋势,且经盐常数校正后的气-水分配系数与挥发速率常数在对数散点图上存在很好的正相关关系。
5) Volatilization rate
挥发率
1.
Testing of volatilization rate for the active ingredient in the combustion of mosquito coil;
蚊香点燃过程中有效成分的挥发率测试
2.
The effect of temperature and time upon the volatilization rate of molybdenum trioxide has been studied.
考察了温度、时间等因素对三氧化钼挥发率的影响。
3.
The quadratic functional relationships between the volatilization rate of continuous casting powder and temperature,Na,CO, content, CaF, content, basicity and time are determined by regression orthogonal design.
通过回归正交设计确定了连铸保护渣基料挥发率同温度、Na2CO3含量、CaF2含量、碱度及时间的二次函数关系式。
6) evaporation rate
挥发速率
1.
Under inert atmospheres and 1473K, the evaporation rate of SnS fromSnO--FeO0-SiO_2 and SnO--FeO--CaO--SiO_2 slags mixed with FeS was investigated by meas-uring the weight loss and composition of samples.
研究表明,在硫化烟化过程中,SnO的挥发与SnS相比可以忽略不计,在炉渣中增加CaO可以加快SnS的挥发速率,挥发的微分速率方程可以表示为: -d(％Sn)/dt=k(％Sn)(％S)其中表观速率常数k分别为4。
2.
Based on the principle of Shell thin-film evaporimeter,an experimetal apparatus and corresponding methods have been established for the determination of the solvent evaporation rates.
参照Shell薄膜蒸发计的原理建立了溶剂挥发速率测定装置,实验测定了纯溶剂在滤纸和铝材上的挥发速率,滤纸上的实验结果与文献数据相比,平均相对误差为3。
补充资料：含锗铁矿鼓风炉挥发提锗
含锗铁矿鼓风炉挥发提锗
extraction of germanium from iron ore containing germanium by volatilization in blast furnace
氧化物和硫化物形态存在。这些锗化物在高温、弱还原气氛下形成易挥发的GeS、GeS:和GeO进入烟尘。通过控制熔炼温度和还原气氛，就可使锗挥发入烟尘得到提取。 含锗铁矿按焦比0.6配入焦炭和一定量熔剂后，加入鼓风炼铁炉内。炉内料柱高1.2~1.6m。鼓入风压2.9一4.4kPa、风量为15m3/min的空气，在1523一1773K温度和控制CO:(CO+COZ)~0.6一0.7弱还原气氛下进行熔炼。在熔炼过程中，炉顶温度控制在873一923K。在此熔炼条件下，铁矿中锗的大部分以Ges、GesZ、Geo的形态挥发入烟气。烟气先经重力沉降器，再进入旋涡除尘器，然后通过空气冷却管道，最后用布袋收尘器收得锗尘。 适当延长鼓风炉的高温区，是提高锗挥发率的关键。控制炉内气氛，则是影响锗挥发率的另一重要因素。炉内气氛的还原性过强，部分铁矿被还原成铁，部分化合态锗也被还原成金属锗，二者形成合金。合金一部分混入炉渣，另一部分沉积于炉缸，从而降低锗的回收率。为达到所需的还原气氛和高的熔炼温度，使作业能连续而顺利地进行，必须造流动性好的渣。如造成分为510:25%~30%、FeO45%一50%、AIZO:10%一15%及CaOS%的渣型，并实施作业区按高度分布的控温制度，使风口高温区延长。收得的重力尘和旋涡尘，可制团后返回鼓风炉熔炼。 含锗0.3%~。.6%的冷却尘和含锗0.6%一1.35%的布袋尘，按烟尘的含锗品位分别经酸浸出后，所得酸浸出母液送萃取、丹宁沉淀、焙烧，或直接送丹宁沉淀、焙烧得锗精矿。锗精矿进一步采用经典氛化法提锗产出Geo:产品。炉渣含锗0.001%一0.002%，选矿后送炼铁厂综合利用。炼得的锗铁合金含锗大于1%，可用电解法或高温氯化法分别回收锗和铁。此法的工艺流程如图。 此法产出的渣量大，约25%的锗随渣流失，挥发过程的锗回收率仅55%左右，成本很高。单纯用含锗一自 酸浸出液一详乖协一二 锗水相丹宁锗一浮中 丹宁锗锗精矿臼 G赶UZ产品 含锗铁矿鼓风炉挥发提锗流程honzhetiekuang gufenglu hu{fa tlzhe含锗铁矿鼓风炉挥发提锗(extraetion ofgermanium from iron ore eontaining ger-manium by volatilization in blast furnaee) 在鼓风炉中于高温、弱还原性气氛条件下熔炼含锗铁矿，使锗挥发进入烟尘的锗回收方法。 中国在1964年前曾用这种方法从含锗铁矿中回收锗。保加利亚、日本和前苏联都用类似方法进行过从含锗铁矿中回收锗的试验研究。 含锗铁矿一般含锗0.003%~0.01%，多以铁矿石为原料提锗，因在经济上不合算，已停止使用。