1)  Anatase TiO_2
锐钛矿型TiO_2
2)  Nanometer anatase titanium oxide
纳米锐钛矿型TiO_2
3)  Anatase TiO_2 nanowires
锐钛矿型TiO_2纳米线
4)  anatase
锐钛
1.
With TiCl 4+O 2 reaction system,the temperature scope in nucleation was discussed from the point of thermodynamics and dynamics during the preparation of ultrafine TiO 2 anatase powder by radio frequency plasma chemical vapor deposition (RF PCVD) method.
制备了平均粒径为 30 nm、用作光催化材料的纯锐钛 Ti O2 超细粉。
5)  anatase
锐钛矿相
1.
Study on Preparation, Modification and Photocatalytic Properties of Anatase Titania Nanoparticles with High Thermal Stability;
高热稳定性锐钛矿相纳米TiO_2的制备、改性及其光催化研究
2.
Pure anatase can be obtained without being sintered by controlling experimental conditions.
通过控制实验条件,可以得到单一的锐钛矿相TiO2纳米晶。
3.
Nanocrystalline anatase TiO2 powders were prepared by the method of precipitation-solution-gelation, using H2TiO3 as re-actants.
温度较低时,锐钛矿相的Raman谱峰明显可见,由于高温下Raman信号减弱,随着温度升高,Raman特征谱峰逐渐减弱以至于全部消失,仅显示出几个宽宽的凸起。
6)  anatase
锐钛矿型
1.
In-situ growth of anatase nano-TiO_2 on cotton fabric and its UV screening property;
锐钛矿型纳米TiO_2在棉织物上的原位生长及其抗紫外线性能
2.
One-step Synthesis of Anatase-Crystalline Titania Hollow Spheres in Aqueous Solution;
水相一步合成锐钛矿型二氧化钛空心球
3.
Then anatase nano-TiO2 powder was calcined at the temperature between 400~1 000 ℃.
在400～1 000℃之间对锐钛矿型TiO2进行煅烧,分析了不同温度处理后样品的晶体结构和光催化活性的变化。
参考词条
补充资料：锐钛矿型钛白
分子式：
CAS号：

性质：以锐钛矿型二氧化钛为主成分的白色颜料。白色粉末二氧化钛含量95%～99%，折射率2.55，密度3.70～3.85g/cm3。吸油量20～24，着色力1300～1350。平均晶体颗粒0.14～0.15μm，比表面积10～14m2/g，莫氏硬度5.5～6，比热容0.71J/(℃·g)。耐化学品，耐高温。

说明：补充资料仅用于学习参考，请勿用于其它任何用途。