1) modified alloy 800
改性800合金
1.
The influence of some processing factors such as cold work and heat treatment on the susceptibility to caustic stress corrosion cracking (SCC) of modified alloy 800, referred to alloy 800M, in a boiling solution of 50%NaOH+0.
通过显微组织检验、拉伸试验、应力分析、C形环应力腐蚀试验、俄歇电子能谱(AES)分析、腐蚀形貌观察,研究了某些加工因素(冷加工和热处理)对国产改性800合金(800M)在沸腾的50%NaOH+0。
2) Alloy 800
800合金
1.
3%SiO2 on SCC of Alloy 800 was investigated using C-ring tests along with anodic polarization measurements for Alloy 800, pure Cr, Ni and Fe.
3％SiO_2溶液中添加Na_2S_2O_3对800合金SCC行为的影响,并结合电化学测量等进行了讨论。
2.
The SCC behavior of Alloy 800 in boiling 50%NaOH solution containing 0.
采用恒电位C形环SCC试验方法,研究800合金在含0。
3.
By examining, the compress stress was seriously generated because of shot peening on the surface of Alloy 800 tubes.
本文用玻璃丸对800合金传热管进行喷丸,明显地改善了它在高温苛性碱溶液中的应力腐蚀性能。
3) Alloy-800
I-800合金
1.
Fretting Wear Behavior of Alloy-800 Tube Materials
I-800合金微动磨损特性研究
2.
The fretting wear behavior of Alloy-800 steam generator tube materials has been investigatded on a Deltalab-Nene7 under normal load(80N),displacement amplitudes (2-80μm) and temperatures(25℃,300℃and 400℃).
使用PLINT高温微动磨损试验机,在法向载荷50N和80N,位移幅值2～80μm,不同温度(25℃、300℃和400℃)条件下,研究了核电蒸汽发生器导热管材料I-800合金的微动磨损特性。
4) 800 nickel-based Alloys
800镍基合金
5) Incoloy 800
因科800镍铬铁高温合金
补充资料：铂改性铝涂层IN738LC耐蚀高温合金热腐蚀产物
铂改性铝涂层IN738LC耐蚀高温合金热腐蚀产物