2) PZT
锆钛酸铅(PZT)
1.
Porous Piezoelecrtric PZT(lead zirconate titanate) ceramics were fabricated by BURPS(Burn-out plastic sphere composites),using flour as the pore-forming agent.
用传统造孔剂燃烧工艺(BURPS)法,以碳化淀粉造粒后为造孔剂,制备了不同孔率的锆钛酸铅(PZT)陶瓷,研究了孔隙率随造孔剂量变化规律,并对其介电性能和压电性能与孔隙率的关系进行了讨论。
2.
A kind of binary system piezoelectric ceramic with good properties was selected to measure its dielectric proprties of the PZT samples at high electrical field.
实验选取一种性能较好的二元系锆钛酸铅(PZT)压电陶瓷配方,通过测试PZT陶瓷样品在强场下的介电性能表明,随着外加电场强度的增大,样品介温曲线的斜率变小;材料的介电损耗随着外加电场的增大而增大,当外加电场从0升至400 V/mm时,介电损耗从0。
3) lead zirconate titanate(PZT)
锆钛酸铅 PZT
1.
Nanopowders of lead zirconate titanate(PZT)are prepared by sol-gel method.
采用溶胶-凝胶法制备了粒径为30~50nm 锆钛酸铅 PZT 纳米压电粉体。
4) lead zirconate titanate (PZT) film
锆钛酸铅(PZT)薄膜
5) PMN-PMS-PZT
铌锰酸铅-锑锰酸铅-锆钛酸铅(PMN-PMS-PZT)
1.
The PMN-PMS-PZT ceramics was prepared by the solid-state,cold isostatic pressing and Gelcasting method respectively and a contrasted study of these preparing methods were carried out.
采用干压、冷等静压和凝胶注模等不同成型工艺制备铌锰酸铅-锑锰酸铅-锆钛酸铅(PMN-PMS-PZT)陶瓷,并进行对比研究。
6) PZT
锆钛酸铅
1.
Effects of compaction process on the density and properties of PZT ceramic;
压制方式对锆钛酸铅压电陶瓷密度及性能影响的研究
2.
Fabrication of PZN-PZT Piezoceramics and Ceramic Fibers;
锌铌酸铅-锆钛酸铅(PZN-PZT)压电陶瓷和陶瓷纤维的制备
3.
The Preparation and Performance Measurement of PZT Film;
锆钛酸铅薄膜的制备及性能测试研究
补充资料:钛酸
分子式:H4TiO4[TiO2·xH2O或Ti(OH)4)]
CAS号:
性质:白色粉末状固体。两性化合物。溶于无机酸及碱类。不溶于水,与强碱反应可生成碱金属偏钛酸盐的水合物。由钛酸盐的盐酸溶液与氨作用后于浓硫酸上干燥而得。用作媒染剂,制二氧化钛等。
CAS号:
性质:白色粉末状固体。两性化合物。溶于无机酸及碱类。不溶于水,与强碱反应可生成碱金属偏钛酸盐的水合物。由钛酸盐的盐酸溶液与氨作用后于浓硫酸上干燥而得。用作媒染剂,制二氧化钛等。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。
参考词条