1) aqueous slurries
水基料浆
1.
The key to this process is prepartion of aqueous slurries of high quality,physical and chemical process of gel-casting.
采用水基料浆注模、凝胶离位复合法制备Al2 O3 /YSZ材料 ,工艺关键是高质量水基料浆的配制、注模和凝胶固化的物理—化学过程的控制。
2.
Results show that shear thinning behaviour and pseudoplasticity of aqueous slurries can be found.
详细研究了固含量、球磨时间、分散剂用量和pH值对8％摩尔分数Y_2O_3稳定ZrO_2水基料浆流变性质的影响。
2) water base slurry
水基浆料
4) cement based grouting material
水泥基注浆材料
1.
The choice of water-cement ratio,the setting time control of cement slurry,the consolidation strength and durability in cement based grouting materials have been studied and experimented.
就水泥基注浆材料中W/C的选择、浆液凝结时间调控、结石强度和耐久性问题进行了试验与探讨,并通过SEM图像从水泥基注浆材料结构上的差异进行了解释,同时提出水泥浆选材用材的建议。
5) cementitious grout
水泥基灌浆材料
1.
Code for application technique of cementitious grout GB/T50448-2008 is the first national standard about application of cementitious grout.
《水泥基灌浆材料应用技术规范》GB/T50448-2008是我国首次编制的关于水泥基灌浆料应用的国家标准,该标准对于促进行业技术进步、保障工程质量、提升国产产品性能将起到重要作用。
6) slurry dewatering
料浆脱水
1.
Selection of slurry dewatering process for wet-process grinding and dry-process burning;
湿磨干烧生产线料浆脱水工艺的选择
补充资料：固体料浆管道
| 固体料浆管道 solids-slurry pipeline 长距离输送浆液的管道。浆液由固体破碎成粉粒状后与适量液体配制而成。现代管道运输中输送的固体主要是煤，此外还有铁、磷、铜、铝矾土和石灰石等矿物，所用液体一般为水。 1914年，英国首次铺设534米长、200毫米直径的铸铁管，输送煤、水各半制成的浆液成功。美国于1957年和1970年分别建成173千米长、254毫米管径的煤浆管道和439千米长、457毫米管径的黑梅萨煤浆管道。1977年巴西建成长393千米、管径为509毫米和460毫米两种的萨马科铁矿浆管道，其最大输量为每年1200万吨。固体料浆管道尚不多。但随着一些技术问题的解决、完善和成熟，固体料浆管道将日益发展。 固体料浆管道的输送工艺包括以下3个步骤。①制浆。将待输的固体破碎到所需粒度范围，并经筛选，组成适当的颗粒级配，再掺水制成浓度适宜的浆液。煤浆液的重量浓度一般在50％左右，铁矿浆液的重量浓度约为66％。②管道输送。根据年输送量选择适宜的管径，确定临界流速，以高于临界流速的速度输送配制好的浆液。因浆液是固液二相的混合物，流态多变。在相同的流速下，当为均质流态时，管道断面上的颗粒均匀悬浮，不会出现固体颗粒沉淀；当为半均质流态时，细颗粒均匀分布在管道断面的上部，大颗粒则在下部，因而下部浓度大，上部浓度小，但也不至于出现固体颗粒沉淀；当为非均质流态时，管道全断面上浓度分布很不均匀，则会出现固体颗粒沉淀，在管道底部形成沉淀层。出现沉淀时的流速为浆液临界流速。只有采用临界流速以上的速度输送浆液，才能使浆液稳定流动，不致形成沉淀层。③固液分离。对由管道输送至末站的浆液进行脱水，分离出固体，然后供给用户。浆液输送过程中，靠增压设备为浆液提供输送动力。 |