1) chemical bath
化学浴
1.
SnS thin films were deposited on glass by the chemical bath deposition method using triethanolamine(TEA),thioacetamide,SnCl_2·H_2O,ammonia(aqeous)as reactants and NH_4Cl(aqeous)as buffer aqeous.
以硫代乙酰胺、三乙醇胺、氯化亚锡和氨水作反应物,氯化铵作缓冲剂,采用化学浴法在玻璃衬底上沉积SnS薄膜,并用X射线衍射(XRD)、扫描电子显微镜(SEM)等分析手段对样品进行了表征。
2.
This paper studies the deposition mechanism of SnS thin film by chemical bath using triethanolamine(TEA),thioacetamide,SnCl_2·2H_2O,ammonia(aqeous) as reactants and using NH_4Cl(aqeous) as buffer aqeous.
研究了以硫代乙酰胺、三乙醇胺、氯化亚锡和氨水作反应物,氯化铵作缓冲剂,采用化学浴法制备SnS薄膜的化学反应机理,分析了络合剂和氯化铵对反应的影响。
3.
SnS thin films were deposited on glass by the chemical bath deposition method using triethanolamine(TEA),thioacetamide,SnCl2·H2O,ammonia(aqeous)as reactant and using NH4Cl(aqeous)as buffer aqeous.
以硫代乙酰胺、三乙醇胺、氯化亚锡和氨水作反应物,氯化铵作缓冲剂,采用化学浴法在玻璃衬底上沉积SnS薄膜。
2) chemical bath deposition
化学浴沉积
1.
Kinetic studies were carried out on the CaWO4 thin films prepared by the chemical bath deposition(CBD).
对化学浴沉积法制备的CaWO4薄膜进行了动力学研究。
2.
ZnO thin films were grown on glass substrate by microwave irradiation assisted chemical bath deposition (MW-CBD).
采用微波辅助化学浴沉积法在玻璃衬底上制备了氧化锌(ZnO)薄膜。
3.
PbSe polycrystalline thin films were synthesized on quartz glass by chemical bath deposition(CBD) with selenourea and selenium,individually.
分别以硒脲和硒粉为Se2-制备剂的主要原料,用化学浴沉积法制备了PbSe多晶薄膜。
3) chemical bath deposition
化学水浴法
1.
ZnS thin films were prepared by chemical bath deposition on common glass substrates.
以普通玻璃作为衬底用化学水浴法制备ZnS薄膜,溶液采用联氨体系。
2.
Effect of different complexing agent on the properties of ZnS thin films for solar cell prepared by chemical bath deposition was studied.
研究了不同络合剂对化学水浴法制备太阳电池用ZnS薄膜性能的影响。
4) chemical bath desposition
化学浴沉淀
1.
By means of chemical bath desposition(CBD),CdS semiconductor material is embedded in the SiO_2 colloidal photonic crystal with different content.
用化学浴沉淀法(CBD)在SiO2胶体晶体中生长了CdS半导体材料,并用UV-VIS-NIR光谱仪和荧光光分度计测试了其光学性能。
5) chemical bath deposition
化学水浴沉积
1.
Research progress on preparation of zinc sulphide thin film by chemical bath deposition;
化学水浴沉积法制备硫化锌薄膜研究进展
2.
Preparation of CdSe film with chemical bath deposition;
化学水浴沉积法制备CdSe薄膜
6) chemical bath deposition
化学浴沉积法
1.
ZnS thin films which are used as buffer layers in thin film solar cell are usually deposited by chemical bath deposition.
太阳能薄膜电池的ZnS缓冲层一般是采用化学浴沉积法制备。
2.
Nano-crystal Cu2S thin films were prepared by chemical bath deposition,with CuSO4·5H2O and Na2S2O3 as precursors,and EDTA as complexing agent.
利用化学浴沉积法,以EDTA为络合剂,CuSO4。
3.
The deposition processes include electrodeposition, microwave-heating and chemical bath deposition.
硫化铅的各种性能与其生长环境以及基片的种类等工艺条件紧密相关,其制备工艺包括了电化学沉积法,微波加热法,以及化学浴沉积法(CBD)等。