1) fiber/whisker
纤维/晶须
1.
This paper mainly describes the toughening of Al_2O_3 ceramic by methods of particle toughening,fiber/whisker toughening,transformation toughening and self-reinforced,and summarize research progress in preparation,toughening mechanism and influencing factors of high fracture toughness Al_2O_3 ceramic.
本文分别通过颗粒弥散相增韧、纤维/晶须增韧、相变增韧、复合增韧以及自增韧等方法对A l2O3陶瓷的增韧研究进行了分类叙述,总结了高韧性氧化铝陶瓷的制备、增韧机理、影响因素的研究进展。
2) whisker/fiber additive
纤维及晶须
3) Cellulose whisker
纤维素晶须
1.
Cellulose whisker(CW) was prepared by hydrolysis of natural microcrystalline cellulose(MCC) with sulfate acid.
采用硫酸酸解天然微晶纤维素(microcrystalline cellulose,简称MCC)制备纳米微晶纤维素晶须(cellulosewhisker,简称CW),加入天然橡胶胶乳共沉后混炼硫化。
4) nano-cellulose whiskers
纳米纤维素晶须
5) mullite whisker(fiber)
多晶莫来石晶须(纤维)
6) Eulaliopsis binata fiber
龙须草纤维
1.
The dyeing property of Eulaliopsis binata fiber was tested and reactive dyes were used here.
就活性染料对龙须草纤维的染色性能进行试验,旨在探索龙须草纤维的基本染色规律。
补充资料：多晶莫来石晶须(纤维)
分子式：
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。