1) Unsteady Casting
非稳态浇铸
1.
Distribution of Inclusion Size in Surface Layer of IF Steel Slab under Unsteady Casting;
非稳态浇铸时IF钢铸坯表层夹杂物粒径的分布
2) unsteady casting
非稳态浇注
1.
The influences of the deoxidizer, reoxidation, unsteady casting and other factors were studied and the main influential factors were found.
通过对杭钢转炉厂Q215钢生产过程各工艺环节系统取样,采用金相显微镜、大样电解和常规化学分析等方法对Q215钢洁净度进行了系统研究,分析了非稳态浇注、二次氧化、脱氧剂等对洁净度的影响,找出了现有生产工艺中影响Q215钢洁净度的主要因素,并提出了相应的工艺改进措施。
2.
The influences of the unsteady casting condition and other factors were studied and the main influential factors were found.
通过对杭钢电炉炼钢厂40Cr钢生产过程各工艺环节系统取样,采用金相显微镜、大样电解和常规化学分析等方法对40Cr钢洁净度进行了系统研究,分析了LF精炼炉、中间包、结晶器、非稳态浇注等对洁净度的影响,找出了现有生产工艺中影响40Cr钢洁净度的主要因素,并提出了相应的工艺改进措施。
3.
The reasons of slab crack under unsteady casting were analysed.
分析了非稳态浇注时导致铸坯裂纹产生的原因,通过采取相应的控制措施,降低了非稳态浇注时铸坯裂纹的发生率。
3) unsteady continuous casting
非稳态连铸
4) static casting
静态浇铸
1.
The effect of electromagnetic stirring on the inner quality of the low carbon steel billet was investigated by static casting experiment.
采用低碳钢进行静态浇铸实验 ,并就电磁搅拌对铸坯内部质量的影响进行了实验研究·实验结果表明 ,电磁搅拌可明显提高铸坯凝固组织的等轴晶率 ,同时又可以改善铸坯内的成分分布状况 ,从而提高铸坯的内部质量·在合理的电磁搅拌参数和浇铸参数条件下能够得到几乎为1 0 0 %等轴晶的铸坯
5) ESR Casting with Liquid Metal
电渣液态浇铸
6) steady versus nonsteady state
稳态/非稳态