1) sheared deficit
剪切缺陷
1.
The results show that the main reasons of crack in the curling process are the serious sheared deficit at the edge of steel plate(steps and fine cracks) and performance variety, such as rigidity ascending、plasticity lowered, caused by cold shearing.
结果表明,钢板板边存在严重的剪切缺陷(台阶和小裂纹)以及由冷剪切引起的性能变化(硬度增高、塑性降低)是导致钢板在卷曲过程中产生裂纹的主要原因。
2) shear,mark
剪切印<玻璃制品缺陷>
3) Splicing defect
剪接缺陷
4) Cutting disadvantages
锯切缺陷
6) collapsibility shear strain
湿陷剪切应变
补充资料：点缺陷(见晶体缺陷)
点缺陷(见晶体缺陷)
point defect
点缺陷point defeet见晶体缺陷。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。