1) closed forming
闭式成形
1.
Gear forming by traditional process of cold extrusion and closed forming are introduced.
介绍了应用闭式成形方法的齿轮成形,同时对闭式成形模具结构、缓冲装置、液压系统等进行了阐述。
2.
The principle and process of spline gear closed forming based on exchanging axles on the common hydraulic press are introduced.
分析了精密圆柱齿轮的冷挤压成形特点,介绍了在普通液压机上基于芯轴交换的圆 柱齿轮闭式成形的基本原理与工作过程、模具结构设计以及模具缓冲与卸荷装置液压系统的 工作原理。
2) fully enclosed die forging
闭塞式成形
1.
An experimental die set with combined female die for isothermal fully enclosed die forging was designed,and the effect of die shape,billet shape and forming force on law of metal deformation and flow was studied by using the simulation experiments.
设计了一套带有组合凹模的等温闭塞式成形试验模具,利用模拟试验方法研究了模具形状、坯料形状和成形力等对金属变性流动规律的影响。
3) Closed-loop forming
闭环成形
1.
The fuzzy control method in multi-point closed-loop forming for 3D curved surface parts;
板类件多点闭环成形的模糊控制方法
4) closed die forming
闭塞成形
1.
The closed die forming is a precision forging technology.
闭塞成形是一种精密模锻技术 ,可以实现锻件的近净成形 ,提高材料利用率、降低成本 ,改善锻件质量 ,是当前国内外十分关注的研究课题。
6) closed type forming
闭式成型
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。