1) Sulfidation roasting
硫化焙烧
1.
The process of chalcopyrite sulfidation roasting is investigated by using of the thermal analytical method and the X-ray diffraction method at lower temperature and with Ar gas protection.
结果表明,黄铜矿硫化焙烧转化为CuS和FeS2的最佳条件为:温度350～400℃;时间4h;粒度-74μm,矿∶硫=10∶1。
2) sulfatizing roasting
硫酸化焙烧
1.
The cobalt in β-naphtholate from can be completely leached by process of acid pickling-oxidizing roasting-sulfatizing roasting-leaching.
采用"焙烧-硫酸化焙烧-浸出"可彻底地将钴从β-萘酚盐中浸出,最佳工艺条件为氧化焙烧温度500~600℃、时间1h,硫酸化焙烧温度600~620℃、时间1h、硫酸用量0。
3) roasting of sulfide ores
硫化矿焙烧
4) oxidizingsulphidizing roasting
氧化-硫化焙烧
1.
If sulphide reagents exist, oxidizingsulphidizing roasting in weak oxidizing atmosphere will benefit FeAsS to decompose and low poison arsenicsulphur compound will form.
当有硫化剂存在时，在弱氧化气氛下进行氧化－硫化焙烧，将有利于ＦｅＡｓＳ分解，并生成毒性低的砷硫化物。
5) magnetized roasting of pyrite
硫铁矿磁化焙烧
6) oxidized roasting of pyrite
硫铁矿氧化焙烧
补充资料：硫化焙烧
硫化焙烧
sulphidizing roasting
!luhuo bershQO硫化焙烧(sulphidizing roasting)矿物原料还原焙烧工艺之一，即难选金属氧化矿加入硫化剂在还原气氛下加热，使有用组分转变为固态金属硫化物(焙砂)的工艺过程。焙砂经物理选矿富集可获得合格精矿。常用的硫化剂为黄铁矿，也可用元素硫、硫酸钠、石膏等。还原剂用粉煤、焦炭。矿石经硫化焙烧处理后，能取得较好的技术经济指标，但此法生产费用较高，应用受到限制。氧化矿的硫化焙烧工艺与还原焙烧相似，只是炉料中需预先混入所需的硫化剂。 (熊志章)