1) C3602 leaded brass
C3602铅黄铜
1.
The mathematic model of predicting C3602 leaded brass hardness after annealing was set up with the help of grey system theory.
利用灰色系统理论建立了C3602铅黄铜退火后硬度预测的数学模型,结果显示在250℃～500℃退火温度范围内,预测值与实测值呈现出较高的吻合性,其相对误差在0。
2) Leaded Brass C3602
C3602黄铜
4) Lead Brass
铅黄铜
1.
Prediction of Superplastic Properties of Lead Brass Based on BP Neural Network;
基于BP神经网络的铅黄铜超塑性能预测
2.
Effects of Modification on As-cast Microstructure and Properties as well as Solidification Mode of Lead Brass in Permanent Mold;
变质处理对铅黄铜铸态组织及凝固方式的影响
3.
The BP network predicting models of lead brass among superplastic tension temperature,initial strain rate and elongation,flow stress were established using the Levenberg-Marquardt method.
借助Levenberg-Marquardt算法,建立了铅黄铜超塑性拉伸温度、初始应变速率与延伸率、流动应力之间的BP网络预测模型,分析了拉伸温度、初始应变速率与延伸率和流动应力之间的关系,得出了铅黄铜最佳的超塑性条件,并以此为依据,进行了铜合金轴承保持架的超塑性成形试验。
5) Pb-brass
铅黄铜
1.
An environmental friendly Bi-brass with cutting-free and excellent properties was developed to substitute for Pb-brass.
研制了一种性能优异的易切削铋黄铜来替代有毒的铅黄铜。
6) binding brass
加铅黄铜
补充资料：铅黄铜
分子式：
CAS号：
性质：在铜锌合金基础上，加入铅的黄铜。按含锌量可分为单相α铅黄铜，两相（α+β）铅黄铜。单相α铅黄铜只能冷轧和热挤，常用的有63Cu-34Zn-3Pb合金，软态的拉伸强度达350MPa，延伸率为45%。具有较高的强度和良好的冷加工性能，有极好的切削性，主要用于仪表和其他机械式仪表上要求切削性极高的零件。两相（α+β）铅黄铜可进行热轧、热挤和冷加工，典型的合金为59Cu-40Zn-1Pb，在550~650℃温度区间具有超塑性，有较高的强度和优良的切削性能，软态的拉伸强度为420MPa，延伸率为45%，是最经济、最常用的铅黄铜。用于制作热矿井和切削加工的零件、螺钉、垫圈、衬套、螺帽、底座、轴承保持器等。
CAS号：
性质：在铜锌合金基础上，加入铅的黄铜。按含锌量可分为单相α铅黄铜，两相（α+β）铅黄铜。单相α铅黄铜只能冷轧和热挤，常用的有63Cu-34Zn-3Pb合金，软态的拉伸强度达350MPa，延伸率为45%。具有较高的强度和良好的冷加工性能，有极好的切削性，主要用于仪表和其他机械式仪表上要求切削性极高的零件。两相（α+β）铅黄铜可进行热轧、热挤和冷加工，典型的合金为59Cu-40Zn-1Pb，在550~650℃温度区间具有超塑性，有较高的强度和优良的切削性能，软态的拉伸强度为420MPa，延伸率为45%，是最经济、最常用的铅黄铜。用于制作热矿井和切削加工的零件、螺钉、垫圈、衬套、螺帽、底座、轴承保持器等。