1) high abrasion furnace carbon black N330
高耐磨炭黑N330
2) HAF
高耐磨炭黑
1.
The rheological property of HAF filled powdered SBR [P(SBR/HAF)] with different addition levels of HAF and aromatic oil during mixing was investigated and compared to that of HAF filled bale SBR (SBR/HAF).
研究了高耐磨炭黑 (HAF)和芳烃油用量对HAF填充型粉末SBR[P(SBR/HAF) ]和块状SBR(SBR/HAF)胶料混炼流变性能的影响。
2.
Moreover,the comparative experiment of the rubber reinforced by CNTs with that by HAF was carried out.
研究了碳纳米管(CNTs)的加入对三元乙丙橡胶(EPDM)复合材料的力学性能和电性能的影响,将CNTs增强EPDM体系的力学性能与高耐磨炭黑(HAF)增强的体系进行了对比,并初步探讨了复合材料的结构。
3) high abrasion furnace black
高耐磨炭黑
1.
Fracture behavior of ethylene-vinyl acetate vulcanizates reinforced by sodium methacrylate or high abrasion furnace black;
甲基丙烯酸钠和高耐磨炭黑增强乙烯-乙酸乙烯酯橡胶的断裂行为
2.
Powdered rubbers containing high abrasion furnace black(HAF) treated with rare earth compounds were prepared by means of coagulation-coprecipitation.
以经稀土化合物处理的高耐磨炭黑和丁腈胶乳为原料,以凝聚共沉法制备粉末丁腈橡胶。
4) Carbon Black N330
炭黑n330
6) super abrasion furnace black
超耐磨炭黑
补充资料：高耐磨炭黑
C 分子量12.01
黑色粉状物。平均粒径27-34nm。比表面积80～110m2／g。氧含量0.5-1.0％。氢含量0．27-0．34％。真密度1．8g／cm3左右。
生产方法 采用燃烧裂解法。即以煤焦油、蓖油和乙烯焦泊为原料，预热混合喷入反应炉，与预热的空气在炉内进行不完全燃烧，裂解生成炭黑炉气，经冷却、分离收集、造粒、筛选、筛选而得。
应用 主要作为填充剂，掺入天然橡胶和多种合成橡胶中，使之具有加工性能良好，分散性好，胶料压出表面光滑的特点，从而可广泛用于生产要求耐磨性能好，抗张强度和伸长率较高的橡胶制品，加高强度运输带、自行车外胎、轮胎胎面胶、胶辊、胶管、胶鞋和电缆包皮等。
黑色粉状物。平均粒径27-34nm。比表面积80～110m2／g。氧含量0.5-1.0％。氢含量0．27-0．34％。真密度1．8g／cm3左右。
生产方法 采用燃烧裂解法。即以煤焦油、蓖油和乙烯焦泊为原料，预热混合喷入反应炉，与预热的空气在炉内进行不完全燃烧，裂解生成炭黑炉气，经冷却、分离收集、造粒、筛选、筛选而得。
应用 主要作为填充剂，掺入天然橡胶和多种合成橡胶中，使之具有加工性能良好，分散性好，胶料压出表面光滑的特点，从而可广泛用于生产要求耐磨性能好，抗张强度和伸长率较高的橡胶制品，加高强度运输带、自行车外胎、轮胎胎面胶、胶辊、胶管、胶鞋和电缆包皮等。