1) oxidized pellet
氧化球团矿
1.
This paper studies crystallization rule of oxidized pellet based on mineralogical compositions and microstructure under different technological conditions.
根据不同工艺条件下焙烧的氧化球团矿的矿物组成和显微结构,研究了氧化球团矿的结晶规律。
2.
Test analysis and studies of green pellet cracking in chain grate and ring in rotary kiln are put forward in a chain grate-rotary kiln production line with oxidized pellet of 2 millions t/a.
通过对200万t/a氧化球团矿链篦机-回转窑生产线链篦机生球爆裂、回转窑结圈的检测分析和试验研究,提出了较为合理的链篦机生球干燥风速和风温,以及链篦机和回转窑温度梯度参数,据此进行了该生产线技术改造和参数调整,有效地解决了链篦机生球爆裂和回转窑结圈问题,使球团生产稳定顺行、能力提高、质量改善、能耗降低,取得了显著的经济效益,为大规模氧化球团矿链篦机-回转窑生产线的设计和生产提供了翔实的技术依据。
2) oxidized pellet
氧化球团
1.
Crystal rule of Fe_2O_3 in oxidized pellet;
氧化球团矿中Fe_2O_3的结晶规律
2.
Microstructure of oxidized pellet mainlymade from hematite with magnetite;
以赤铁矿为主配加磁铁矿制备的氧化球团矿显微结构
3.
The test production aspect of 200Mt/a grate-kiln oxidized pellet production line in HANGANG, and the process characteristics and chief equipments were presented in this paper.
介绍了邯钢200万t/a链篦机回转窑酸性氧化球团生产线的工艺特点和主要设备,以及建成投产后试生产的有关情况。
3) Acid Pellet
氧化球团
1.
Technical Transformation of 1.2 Million Ton Acid Pellet Project in Liugang;
柳钢120万吨氧化球团工程的技术改造
2.
A laboratory test of preparation of acid pellet using Manaoshan concentrate as raw material was carried out.
以玛瑙山磁铁精矿为原料 ,进行了制备氧化球团的成球、焙烧和冶金性能等试验研究。
4) Oxidized pellets
氧化球团
1.
Experimentally, the authors study the pelletizing properties of the iron concentrate and the roasting and metallurgical properties of the iron concentrate's oxidized pellets.
以程潮磁铁精矿为原料、膨润土为粘结剂 ,制作了氧化球团矿。
2.
There are many efficient methods to use cinder application,including preparation of high grade magnetite,producing oxidized pellets,being reduced to iron directly and so on.
利用硫铁矿烧渣制备高品位磁铁矿、生产氧化球团、直接还原制备生铁等是综合利用硫铁矿的有效途径。
5) Oxide pellet
氧化球团
1.
Aimed at decreasing the addition amount of bentonite in oxide pellet produc-tion process, the pelletizability of some kinds of bentonite, organic binder and organic/inor-ganic complex binder were tested.
从粘结剂与精矿粉的混合效果、成品球的质量和成本综合考虑，氧化球团采用复合粘结剂是最佳选择。
2.
Measures of enhancing the strength of preheated and fired oxide pellet with organic binder were put forward in order to solve this problem.
针对有机粘结剂在我国氧化球团生产应用中存在的预热焙烧球强度低、无法满足我国生产要求的问题,进行了提高有机粘结剂氧化球团矿强度的研究。
3.
Study on the mechanism provide theoretical support for preparation of oxide pellets and promote the development of the technology.
氧化球团法处理转炉污泥作为新利用途径具有广阔的发展前景。
6) MgO pellets containing fluorine
含氟氧化镁球团矿
补充资料：球团矿
球团矿
pellet
q一utuankuang球团矿(pellet)将细粒度的铁精矿配入少量球团私结剂，经过造球与焙烧制成的球状炉料。它和烧结矿并称为人造富矿。主要作为高炉炼铁的原料，也可以作为直接还原铁及熔融还原铁的原料，在炼钢过程中可作为氧化剂及冷却剂使用。 类别球团矿按化学成分主要有酸性球团矿和自熔性球团矿两大类。酸性球团矿的主要矿物为赤铁矿，脉石成分以酸性的510:为主，含碱性物质cao，MgO极少;自熔性球团矿的主要矿物为赤铁矿，脉石成分除510:外含有较多的CaO，碱度(CaO/510。)一般在0.8一1.2之间。此外为了改善球团矿的高温冶金性能，在球团原料中添加橄榄石、白云石、煤或预还原处理，分别获得橄榄石球团矿、白云石球团矿，多孔球团矿和预还原球团矿。球团矿按其固结方式可分为焙烧固结球团矿和冷固结球团矿。前者在高温下(1200一1300℃)以Fe203的再结晶与晶粒长大使球团矿具有很高的强度，后者以各种豁结剂把铁精矿固结起来，如水玻璃、腐殖酸钠、纸浆废液、膨润土等，或者以细磨的高炉水、渣、波特兰水泥、消石灰等形成水化硅酸盐的微晶，使球团矿具有一定的强度。世界上90%以上的球团矿是高温焙烧固结的。 性能球团矿的强度高(单个球的抗压强度达Z000N以上)，转鼓指数可达95%(150标准)，可以长期贮存和长途运输，它的粒度均匀(一般为9一12.smm)，颗粒间孔隙度大，透气性好。球团矿的气孔率高(2。%以上)，且多为均匀分布的开口微气孔，加之主要矿物为赤铁矿，故还原性好。球团矿在氧化性气氛下焙烧，因而兼有除硫作用，一般球团矿含硫很低。由于球团矿不是依靠液相来固结的，可以使用含铁量很高的铁精矿作为原料，生产出品位高、杂质少的优质人造富矿。 (孔令坛)