1)  Vinyl acetate-acrylate copolymerization emulsion
乙丙乳液
2)  vinyl acetate emulsion
乙丙乳液
1.
Based on vinyl acetate, epoxy resin, n-butyl acrylate as main monomers, and α-Methylacrylic as functional monomer, vinyl acetate emulsion modified with epoxy resin by semi-continuous emulsion polymerization is prepared.
采用醋酸乙烯酯、E-44环氧树脂、丙烯酸丁酯作为主单体,以α-甲基丙烯酸作为官能单体,采用半连续乳液聚合工艺,制备了环氧改性乙丙乳液。
3)  acetate ethylene propylene ester emulsion
环氧乙丙乳液
4)  vinyl acetate-carylic emulsion coating
乙-丙乳液涂料
5)  epoxy modified vinyl acetate/acrylic emulsion
环氧改性乙丙乳液
1.
The formulations, production technology and technical specifications of the epoxy modified vinyl acetate/acrylic emulsion and the latex paint based on it were given.
采用特殊的乳化工艺使环氧树脂与醋酸乙烯、丙烯酸单体混溶进行共聚改性，所得的环氧改性乙丙乳液克服了乙丙乳液的缺点。
6)  ethylene-propylene rubber
乙丙橡胶
1.
Production and market of ethylene-propylene rubber;
乙丙橡胶的性能和应用需求
2.
Production technology and market status of ethylene-propylene rubber;
乙丙橡胶生产、供需和技术概况及价格分析
参考词条
补充资料：乙丙乳液
    乙丙乳液又称醋丙乳液，是由醋酸乙烯与丙烯酸酯等单体共聚而得。白色乳状液体，相对密度1．0l0～1．020，总固含量40%～50％。粘度l 50mPa·s，ph值5～6，残留单体含量＜0.5％，表面张力(20℃)45．2mN／m，平均粒径0.20～0.25um，玻璃化温度约10 ℃，最低成膜温度5～10℃。化学稳定性(5％NaOH、5％HCl、5％CaCl2)24h无变化，热稳定性80 ℃／24h无变化，冷冻稳定性-5℃／24h无变化。贮存稳定性1年不分层、不凝聚。胶膜拉伸强度9．4MPa，胶膜吸水性30h 2．5%～3．5％。乙丙共聚乳液具有很好的耐水性、柔韧性。
    用作无纺布、地毯胶粘剂，也用于改进白乳胶的耐水性，用于制造建筑密封胶。