1) twisting formation
扭曲成形
1.
And meanwhile, two kinds of twisting formation devices are introduced, which could serve as a reference for the design and manufacture of similar multi-position progressive dies.
针对压力臂的技术要求,确定了合理的排样方案,阐述了该级进模设计特点及要点,同时,还介绍了两种扭曲成形装置,可供类似多工位级进模的设计、制造作参考。
2) distortion cost
扭曲成本
1.
Under asymmetric information,the models explain the free-riding behavior of the members in R&D entity by introducing variables of distortion cost and social benefit.
基于信息不对称条件,通过引入社会扭曲成本与社会收益变量,解释了合作体成员可能出现的搭便车行为,并构建了互补性研发体成员在政府不同激励工具下的决策模型。
3) distortion
[英][dis'tɔ:ʃən] [美][dɪs'tɔrʃən]
扭曲变形
1.
Through the practice we can reach a conclusion that distortion will take place when a hyperb.
冷却塔起爆后在空中经过短暂的扭曲变形,最后按预计方向倒塌在安全范围内,破碎效果良好,爆堆高度只有4—5m,达到了预期的爆破效果。
2.
In this article, a question is discussed on the deflexion and distortion of boom in advanced development of R series digging machine.
本文针对R系列挖掘机试制中动臂扭曲变形问题,根据窄长形状结构件装配质量不好,焊接工件摆放位置不当,以及焊接顺序、方向不合理易造成结构件焊后产生扭曲变形的理论,对动臂焊接翻转胎具进行了改进,并提出了对动臂焊前姿态、焊接顺序、焊接方向、焊接过程的热对称以及焊接间断时间等进行整体调整和控制措施。
4) twist distortion
扭曲形变
5) dished
[英][diʃt] [美][dɪʃt]
凹形扭曲
6) domed
[英][dəʊmd] [美][domd]
凸形扭曲
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。