1) multi-stage hot compression deformation
多道次热压缩变形
2) two-stage hot compression deformation
两道次热压缩变形
3) multi-pass hot deformation
多道次热变形
1.
The flow stress and static softening behaviors have been investigated during multi-pass hot deformation by isothermal interrupted hot compression.
通过对幂指数应力函数中系数A和β与应变关系的分析,以及采用平均软化法考虑前一道次变形的残余应变对后一道次变形的影响,建立了2195铝锂合金多道次热变形的流变应力方程。
2.
The microstructure evolution of Q235 plain carbon steel in multi-pass hot deformation was investigated by means of hot compression simulation.
利用热模拟压缩变形实验研究了Q235碳素钢多道次热变形及后续处理过程的组织演变规律。
4) hot compression deformation
热压缩变形
1.
Flow stress behavior of 5083 aluminium alloy under hot compression deformation;
5083铝合金热压缩变形流变应力行为
2.
The flow stress during hot compression deformation of Al-Mg-Si-Cu alloy;
Al-Mg-Si-Cu合金在热压缩变形中的流变应力
3.
Flow stress behaviors of spray-deposited 5A06 aluminum alloy under hot compression deformation;
喷射沉积5A06铝合金热压缩变形的流变应力行为
5) hot compressive deformation
热压缩变形
1.
The hot compressive deformation behaviour of superalloy GH674 was investigated in the temperature range from 950 to 1200 and at strain rate range from 0.
结果表明,在试验研究的变形条件下,GH674型高温合金在热压缩变形过程中发生明显的动态再结晶;用Zener-Hollomon参数的指数函数能较好地描述该合金高温变形时的流变行为;所获得的峰值应力热变形方程为σp=21。
2.
The effect of precipitates on hot compressive deformation behavior has been investigated.
1Al合金进行了室温~800℃范围内的热压缩变形试验,应变速率0。
6) hot compression
热压缩变形
1.
Model for flow stress of Inconel 751 alloy under hot compression;
Inconel 751合金热压缩变形条件下的流变应力模型
2.
Study on flow stress of Mg-3Al-1Zn-0.8Nd alloy at hot compression;
Mg-3Al-1Zn-0.8Nd合金热压缩变形流变应力的研究
3.
Flow stress behavior of Al-Mg-Sc alloy during hot compression
Al-Mg-Sc合金热压缩变形的流变应力行为
补充资料：高温压缩永久变形试验
分子式：
CAS号：
性质：考察橡胶制品在高温压缩状态下永久变形的试验。测定时将试样进行一定压缩后，放在高温下保持一段时间，然后在室温下冷却2h，除去负荷后再自由恢复1h，最后测定试样高度，高温下压缩永久变形率K由下式计算。式中，h0、h1、h2分别为压缩前压缩下和恢复后的试样高度。
CAS号：
性质：考察橡胶制品在高温压缩状态下永久变形的试验。测定时将试样进行一定压缩后，放在高温下保持一段时间，然后在室温下冷却2h，除去负荷后再自由恢复1h，最后测定试样高度，高温下压缩永久变形率K由下式计算。式中，h0、h1、h2分别为压缩前压缩下和恢复后的试样高度。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条