1) Silver phosphate
磷酸银
1.
The results show that the glazed ceramic tiles has excellent antibacterial action, whiteness, glaze fit, and other properties, by adding 2% of silver phosphate, 5%of phosphatic calcium, and biscuit firing at 1?130?℃,fritting at 1?050?℃.
结果表明 :素烧温度 1130℃、釉烧温度 10 5 0℃ ,釉料中添加磷酸银 2 %、磷酸钙 5 %可获得良好的抗菌性能 ,各项指标均达到国家标准。
2.
Keeping its quality in accordance with the National Ceramics Standard, better sterilizing effectiveness of this ceramics can be achieved by adding 3% of silver phosphate and heating at 1100℃.
在烧成温度１１００℃下，添加磷酸银３％、硫酸铜７％，可获得各种性能达到日用瓷标准要求并有较好杀菌效果的杀菌陶
3.
By adding silver phosphate as antibacterial into the batch of borosilicate glass,we can get the anti-bacterial glass in high temperature melting furnace.
采用高温熔融法,在硼酸盐玻璃的配合料中引入抗菌剂磷酸银,一次烧制而成制得抗菌玻璃材料。
2) silver orthophosphate
正磷酸银
3) silver pyrophosphate
焦磷酸银
4) silver metaphosphate
偏磷酸银
5) Ag_xNa_yH_1-x-yZr_2(PO_4)_3
磷酸锆银钠
6) silver-loaded zirconium phosphate
载银磷酸锆
1.
Study on La_2O_3 doped silver-loaded zirconium phosphate and its antibacterial EVA foamed materials;
La_2O_3掺杂载银磷酸锆及其抗菌EVA发泡材料的研究
2.
The surface modification effect of silver-loaded zirconium phosphate was evaluated by FT-IR and viscosity measurement.
以载银磷酸锆为抗菌剂,铝酸酯偶联剂为改性剂,乙烯-醋酸乙烯共聚物(EVA)树脂为基本原料,制备抗菌EVA发泡材料。
3.
Using silver-loaded zirconium phosphate as an antibacterial agent, glycerol monostearin, oleic amide as the modifiers and linear low density polyethylene (LLDPE) as the carrier resin, antibacterial master batch were prepared by means of interfacial modification, twin-screw extrusion blow molding.
以载银磷酸锆为抗菌剂,硬脂酸单甘油酯、油酸酰胺为改性剂,LLDPE为载体树脂,通过界面改性、双螺杆挤出切拉方法制备抗菌母粒,按设计比例添加到聚乙烯树脂中,采用吹塑成型工艺制备抗菌聚乙烯薄膜。
补充资料：磷酸银
化学式Ag3PO4，分子量418.58。黄色立方晶体。密度6.370g/cm3，熔点849℃，加热或在日光照射下变为棕色。溶于硝酸、氨水、氰化钾，微溶于水。用于制溴化银、碘化银乳剂。由硝酸银溶液跟磷酸钠溶液反应制得。