1) Oscillating Packing Injection Molding
动态保压注射成型
1.
Study of Reinforcing and Toughening of HDPE/m-LLDPE Blends by Oscillating Packing Injection Molding;
共混体系HDPE/m-LLDPE在动态保压注射成型中增强增韧的研究
2) oscillation packing injection molding
动态保压注射
1.
Various vibration molding techniques, including oscillation packing injection molding, shear vibration injection molding, and pressure vibration injection molding were introduced.
对本课题组多年来进行的动态保压注射成型、剪切振动注射成型和压力振动注射成型研究进行了简要总结。
3) dynamic injection molding
动态注射成型
1.
The maximum tensile strength of composite by dynamic injection molding is increased by 11.
与稳态注射成型的复合材料相比,动态注射成型复合材料的拉伸强度最大可提高11。
2.
Taguchi method was used to optimize the processing parameters of mold filling of dynamic injection molding and explore the relationship between processing conditions and the physical properties of isotactic polypropylene.
运用了Taguchi方法研究了PP动态注射成型工艺参数对制品性能的影响。
3.
The flow behavior of polymer in the cylindrical runner under the field of the axial vibration force during the course of electromagnetic dynamic injection molding was studied.
研究了聚合物电磁动态注射成型过程中熔体在轴向振动力场作用下在圆柱形流道中的流动情况。
4) the oscillating packing injection moldings
动态保压成型装置
6) colloidal injection moulding
胶态注射成型
1.
Key technique and equipment on colloidal injection moulding of high reliability ceramic;
高可靠性陶瓷部件胶态注射成型关键技术及装备
补充资料：注塑成型之保压压力
保持压力的设定是为使树脂在冷却的过程中不致产生回流，且能继续补充因树脂冷却收缩而不足的空间，而得到最佳的模具复制效果。 保持压力设定过高，易造成毛边、过度充填浇口附近的应力集中等不良现象，保持压力设定过低，又易造成收缩太大、尺寸不安定等现象。
保持压力必须伴随保压切换点及保压时间设定方为有效。
保压不足时会导致：1.凹陷；2.气泡；3.收缩率增加；4.成形品尺寸变小；5.尺寸的波动性变大；6.由于熔胶回流导致内层配向。
过大的保压则会造成：
1.注道(Sprue)区域的应力；
2.脱模困难；
3.外皮层的拉伸应力。
保压时间阶段逐次降低保压可（多段保压）：
1.减少翘曲、降低从 浇口到末端的成形品区域之收缩变异；
2.减少内应力；
3. 减少能源损耗。
保持压力必须伴随保压切换点及保压时间设定方为有效。
保压不足时会导致：1.凹陷；2.气泡；3.收缩率增加；4.成形品尺寸变小；5.尺寸的波动性变大；6.由于熔胶回流导致内层配向。
过大的保压则会造成：
1.注道(Sprue)区域的应力；
2.脱模困难；
3.外皮层的拉伸应力。
保压时间阶段逐次降低保压可（多段保压）：
1.减少翘曲、降低从 浇口到末端的成形品区域之收缩变异；
2.减少内应力；
3. 减少能源损耗。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。