1) PA66/LLDPE blends
PA66/LLDPE共混物
2) PA66/irradiated LLDPE blends
PA66/辐照LLDPE共混物
3) PTFE/PA66 blends
PTFE/PA66共混物
1.
The effects of PTFE content on water-absorptivity,notched impact strength and complex viscosity of PTFE/PA6 and PTFE/PA66 blends were investigated by water immersion test,Charpy impact fracture test and dynamic rheology measurement in this paper.
通过浸水实验、缺口冲击断裂实验和动态流变测试,考察了PTFE含量对PTFE/PA6和PTFE/PA66共混物的吸水率、冲击断裂强度及熔体黏度的影响以及熔体黏度随温度和频率的变化规律。
4) PA66/PP blend
PA66/PP共混物
1.
The influence of POE-MAH on the morphological structure and the compatibilily of PA66/PP blends was studied by SEM, DSC and WAXD.
通过扫描电镜(SEM)观察、差示扫描量热法(DSC)和广角X射线衍射分析(WAXD),研究了POE-MAH对PA66/PP共混物的形态结构和相容性的影响。
5) PET/PA66 Blends
PET/PA66共混物
6) PA66/PTFE blends
PA66/PTFE共混物
1.
PA6/PTFE and PA66/PTFE blends with different PTFE contents are prepared by melt blending in twin-screw extrusion process, in which PA6 and PA66 are the continuous phase and PTFE is the dispersed phase.
本工作以PA6和PA66为连续相,以PTFE为分散相,采用双螺杆挤出熔融共混技术制备了不同比率的PA6/PTFE和PA66/PTFE共混物,利用60Co-γ射线源,以不同辐照剂量(20kGy、50kGy和100kGy)对这两个材料体系进行了γ辐照。
补充资料：PA66
分子式： [CO(CH2)4CONH(CH2)6NH]n
CAS号：
性质：又称聚酰胺66(polyamide 66)或尼龙66(nylon 66)。微黄半透明或乳白色不透明树脂。相对密度1.14～1.15，熔点259～267℃。耐磨、耐油、自润滑性优良，耐热性、强度、刚性是脂肪族尼龙中最高的品种。拉伸强度75.9～82.9MPa，压缩强度91MPa，悬臂梁冲击强度(缺口)4kJ/m，热变形温度(1.82MPa)75℃，硬度R120，体积电阻率1015Ω·cm，介电强度35kV/mm，自熄。由己二酸和己二胺缩聚反应制得。可挤塑、注塑、吹塑等方法成型加工。可增强、填充、合金化改性。大量用作纤维、轮胎帘子线、广泛用于车辆零部件、电气零部件和耐磨耐油零部件。
CAS号：
性质：又称聚酰胺66(polyamide 66)或尼龙66(nylon 66)。微黄半透明或乳白色不透明树脂。相对密度1.14～1.15，熔点259～267℃。耐磨、耐油、自润滑性优良，耐热性、强度、刚性是脂肪族尼龙中最高的品种。拉伸强度75.9～82.9MPa，压缩强度91MPa，悬臂梁冲击强度(缺口)4kJ/m，热变形温度(1.82MPa)75℃，硬度R120，体积电阻率1015Ω·cm，介电强度35kV/mm，自熄。由己二酸和己二胺缩聚反应制得。可挤塑、注塑、吹塑等方法成型加工。可增强、填充、合金化改性。大量用作纤维、轮胎帘子线、广泛用于车辆零部件、电气零部件和耐磨耐油零部件。