2) ferrite grain
铁素体晶粒
1.
013%Nb)in solution can make ferrite grain finer and then yield strength increased by 55 MPa in .
013%)能使铁素体晶粒细化,造成钢的屈服强度平均提高55 MPa。
2.
The changing principle, which after r→Q phase change large or small of ferrite grain is changed with .
本文就热变形工艺参数对ＤＨ３６热轧船板用钢组织变化规律进行了模拟研究，总结了γ→ａ相变后铁素体晶粒大小随变形量、终轧温度、冷却速度的变化规律，并借此讨论了ＤＨ３６钢控轧控冷工艺。
3) ultra-fine grained ferrite
超细晶粒铁素体
4) ferrite grain size
铁素体晶粒尺寸
1.
Double experiments of controlled rolling/cooling process were carried out on a lab mill and the results showed that the effect of ferrite grain size on the mechanical properties is greater than that of pearlite morphology for the low-carbon cold heading steel.
对低碳铆螺钢采用两次控轧控冷试验,结果表明,铁素体晶粒尺寸比珠光体形态对低碳铆螺钢力学性能的影响要大。
2.
A study on effect of reversing cold rolling on texture and ferrite grain size of DX51D(LCAK steel) and DX54D(IF steel) has been done by simulating experiment of reversing and continuous cold rolling and annealing in the laboratory.
在实验室通过可逆式和连续式冷轧及退火模拟试验,研究了可逆式冷轧对DX51D(低碳铝镇静钢)和DX54D(无间隙原子钢)钢板织构及铁素体晶粒尺寸的影响。
6) equiaxed ferritic grain
等轴铁素体晶粒
补充资料：低温铁素体钢
分子式：
CAS号：
性质：适合低温(273～153K)使用的低合金铁素体钢。它们在脆性转变温度以上使用。可为三类：(1)低碳-锰钢，如233K用钢16Mn属于此类；(2)低镍钢，在233～213K用0.5％Ni钢；当温度降至193～183K时，用2.25％Ni钢，或含锰的1.5％Ni钢；(3)无镍铬低温铁素体钢，主要有203K用钢09Mn2V及09MnTiCuRE，183K用钢06MnNb，153K用钢06AlCu和06AlNbCuN。低温铁素体钢主要用于液体丙烷与丙烯、液氨等液化气的储存及输送装置，寒冷地区野外作业的设备和工程结构以及一些冷冻设备等。
CAS号：
性质：适合低温(273～153K)使用的低合金铁素体钢。它们在脆性转变温度以上使用。可为三类：(1)低碳-锰钢，如233K用钢16Mn属于此类；(2)低镍钢，在233～213K用0.5％Ni钢；当温度降至193～183K时，用2.25％Ni钢，或含锰的1.5％Ni钢；(3)无镍铬低温铁素体钢，主要有203K用钢09Mn2V及09MnTiCuRE，183K用钢06MnNb，153K用钢06AlCu和06AlNbCuN。低温铁素体钢主要用于液体丙烷与丙烯、液氨等液化气的储存及输送装置，寒冷地区野外作业的设备和工程结构以及一些冷冻设备等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。