2) glass infiltrated alumina ceramics
玻璃渗透氧化铝陶瓷
1.
The fabrication process of glass infiltrated alumina ceramics(in-ceram alumina) was investigated,such as changing powder/liquid ratio,pre-sintered temperature and forming method.
通过改变氧化铝粉浆的粉液比、预烧温度以及成型工艺等参数,研究了以上因素对用于制作全瓷冠桥的In-Ceram玻璃渗透氧化铝陶瓷复合体性能的影响。
2.
The fabrication process of glass infiltrated alumina ceramics (CAD/CAM&In-ceram alumina),such as solid loading,presintered temperature and forming method,was investigated.
研究了氧化铝粉浆的固相含量及预烧温度、氧化铝基底块体成形工艺对用于制作全瓷冠桥的计算机辅助设计/加工(CAD/CAM)&In-Ceram玻璃渗透氧化铝陶瓷复合体性能的影响。
3) alumina glass-infiltrated ceramic
氧化铝玻璃渗透陶瓷
4) glass-alumina
玻璃-氧化铝
1.
In this article, glass-alumina functionally graded materials were prepared by rapid prototyping technology.
利用快速成形技术制备玻璃-氧化铝梯度功能材料,所用原料为Na2O-CaO-SiO2玻璃和氧化铝粉。
2.
In this article,present research progress of glass-alumina functionally gradient materials(FGMs) is reviewed,included preparation methods and properties of FGMs.
从制备方法及梯度材料的性能两方面,阐述了目前玻璃-氧化铝功能梯度材料的研究进展。
5) glass infiltration
玻璃渗透
1.
Study on the glass infiltration speed of dental CAD/CAM alumina with different temperature;
不同温度下牙科CAD/CAM用氧化铝玻璃渗透速率的测定
6) infiltration glass
玻璃渗透
1.
Methods: Infiltration glass powder with different content of cerium oxide (1%～4%) were fabricated.
结果 :经玻璃渗透后 ,氧化铝玻璃复合体的b 值与比色板的b 值范围吻合较好。