1) reject fly ash
粗粉煤灰
1.
By means of the tests of compressive strength, toxicity characteristic leaching procedure(TCLP) and dynamic leaching test(DLT), it was studied that the feasibility of solidification and stabilization (S/S) of heavy metals using reject fly ash (rFA).
利用强度发展、毒性浸出试验(TCLP)和动态浸出试验(DLT)等手段探讨了废弃粗粉煤灰水泥系统固化/稳定含铅、铜和锌的重金属废弃物的可能性。
2.
Compared with the influence of different chemical activators on the strength development, hydration degree of reject fly ash and hydration products, it can be found that the addition of Na 2SO 4 and K 2SO 4 can significantly increase the compressive strength at both early and later curing ages.
通过研究不同化学激发剂对废弃粗粉煤灰 -水泥系统的强度发展、水化程度、水化产物等的影响 ,发现掺入Na2 SO4 和 K2 SO4 可以大幅提高废弃粗粉煤灰 -水泥系统在早期和晚期的抗压强度 ,而掺入 Ca Cl2 和 Ca(OH) 2 的效果则不明显 ,X射线衍射的测试结果也证明了这一点。
3.
Comparing the influence of chemical reagents-Na 2SO 4 and K 2SO 4 on the strength development,hydration degree and porosity of reject fly ash blended cement pastes,it is found that the addition of these two chemical reagents can increase the compressive strength significantly at both early and later curing stages.
通过研究碱式硫酸盐对废弃粗粉煤灰 -水泥系统的强度发展、水化程度及样品孔隙率等的影响 ,发现掺入Na2 SO4 和 K2 SO4 可以大幅提高废弃粗粉煤灰 -水泥系统在早期和晚期的抗压强度 ,在试验条件下 ,掺 Na2 SO4 的最佳掺量为总重量的 6 % ,K2 SO4 的最佳掺量为总重量的 4 % ,这些最优掺量都与激发剂的溶解度有关。
2) pulverized fuel ash [PFA]
粉煤灰;煤灰
3) pulverized fuel ash (PFA)
粉煤灰;飞灰;煤灰
4) lime fly ash
石灰粉煤灰
1.
Mixing ratio design and construction technology of lime fly ash stabling macadam base
石灰粉煤灰稳定基层配合比设计及施工工艺
2.
However, the mixture of lime fly ash stabilizing phosphorous slag has high strength, which can be used as the base of expressway.
磷渣不宜用水泥或石灰单独进行稳定 ,用石灰粉煤灰稳定磷渣 ,能获得较高的强度 ,其 7d强度满足高速以及一级公路二灰稳定类基层强度要求。
3.
The comprehensive investigation into the interaction characteristics of 5 kinds of domestic geosynthetics with sand and lime fly ash was presented by pull out tests.
以5种不同种类的国产土工合成材料为加筋材料,以砂和石灰粉煤灰为填料,比较了各种土工合成材料与填料的界面作用特性,试验表明:(1)石灰粉煤灰自重较轻,摩擦角高,并且比砂的拉拔系数相对偏高一倍左右,是理想的土工合成材料加筋土工程的填料;(2)土工合成材料的拉拔系数从高到低排序为涤纶纤维经编土工格栅最高,塑料拉伸土工格栅次之,土工网较低,土工织物最低;(3)不同填料、不同土工合成材料的拉拔系数相差较大,具体加筋土工程采用的拉拔系数需要通过拉拔试验确定。
5) tail flyash
粉煤灰尾灰
1.
This article describes the study and application of new continuous production process of tail flyash in our company.
通过对环保产品粉煤灰尾灰连续性生产新工艺的研究及在我公司的开发应用情况介绍 ,为粉煤灰产品加工提供了一条新的工艺路线及途径 ,用电站的粉煤灰尾灰生产的粉煤灰尾灰产品达到了较好的质量 ,并取得了良好的社会效益、环保效益与经济效益。
补充资料：粉煤灰硅酸盐水泥
分子式：
CAS号：
性质：由硅酸盐水泥熟料、粉煤灰、适量石膏磨细制成的水硬性胶凝材料，代号P·F，中国主要水泥品种之一。粉煤灰掺加量为20％～40％(wt)，标号分275、325、425、425R、525、525R、625R七个等级。性能和火山灰水泥相似，但需水性及干缩性较小，抗裂性较好，水化热较低，抗蚀性也较好。适用于一般的工业和民用建筑，尤其适用于大体积水工混凝土以及地下和海港工程等。
CAS号：
性质：由硅酸盐水泥熟料、粉煤灰、适量石膏磨细制成的水硬性胶凝材料，代号P·F，中国主要水泥品种之一。粉煤灰掺加量为20％～40％(wt)，标号分275、325、425、425R、525、525R、625R七个等级。性能和火山灰水泥相似，但需水性及干缩性较小，抗裂性较好，水化热较低，抗蚀性也较好。适用于一般的工业和民用建筑，尤其适用于大体积水工混凝土以及地下和海港工程等。