1) artificial accelerated aging test
人工加速老化实验
2) accelerated ageing
加速老化，人工老化;加速实效
3) artificial accelerated ageing test
人工加速老化试验
1.
This paper contrastively analyzes the field exposure test and artificial accelerated ageing test data in the South China Sea about the fluorocarbon coatings for the anticorrosion engineering of Main Gymnasium of Olympic Games and other fluorocarbon coatings, giving the, differences among every type of fluorocarbon resin coatings about their aging-resistance.
介绍了奥运主体育场"鸟巢"防腐工程用氟碳涂料与其它类型氟碳树脂涂料在海南的天然曝晒试验数据与人工加速老化试验数据对比分析,并详细阐述了各种类型氟碳树脂涂料在耐老化性方面存在差异的原因。
2.
The photo-oxidation ageing process of polypropylene filaments was studied by artificial accelerated ageing test using different intensities of UV irradiation.
以聚丙烯长丝为对象,采用不同紫外线辐射强度的人工加速老化试验对其光氧老化过程进行研究。
4) artificial weathering test
人工气候加速老化试验
5) accelerated aging test
加速老化试验，人工老化试验
6) accelerated aging tests
加速老化实验
补充资料：耐人工加速老化性
分子式：
CAS号：
性质：是基于大量的天然曝露试验的结果，在实验室内人为地模拟气候的种种破坏因素，并给予一定的强化，以克服天然曝露试验需时过长的不足。强化包括光源（日光以紫外线灯代替，紫外线区的光线对材料的破坏性最大），温度（温度升高也促使漆膜加速老化），湿度（使紫外线照射的破坏作用增强），氧气（氧化作用促进老化引起的漆膜龟裂、漆膜失光）等方面。强化包括以紫外线光代替日光；以高温高湿代替常温常湿，以氧气代替空气，这些都可加速对漆膜的破坏，在短期内得到结果，但人工加速老化试验往往与天然曝晒试验的结果不完全一致，但在没有更好的办法之前，这仍不失为研究涂膜耐老化性能的一个捷径。
CAS号：
性质：是基于大量的天然曝露试验的结果，在实验室内人为地模拟气候的种种破坏因素，并给予一定的强化，以克服天然曝露试验需时过长的不足。强化包括光源（日光以紫外线灯代替，紫外线区的光线对材料的破坏性最大），温度（温度升高也促使漆膜加速老化），湿度（使紫外线照射的破坏作用增强），氧气（氧化作用促进老化引起的漆膜龟裂、漆膜失光）等方面。强化包括以紫外线光代替日光；以高温高湿代替常温常湿，以氧气代替空气，这些都可加速对漆膜的破坏，在短期内得到结果，但人工加速老化试验往往与天然曝晒试验的结果不完全一致，但在没有更好的办法之前，这仍不失为研究涂膜耐老化性能的一个捷径。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。