1) original structure
原始组织
1.
By means of high temperature microscope,graphite precipitation from T10A steel specimens with 4 kinds of original structures has been dynamicly observed when heated and cooled in vacuum.
用高温金相显微镜动态观察4种原始组织的T10A钢试样在真空加热及冷却时的石墨析出现象。
2.
The results show that the original structure affects the microstructural evolution process in a great extent.
研究了控制浇注法制备A356合金半固态枝晶衍变规律,结果表明:原始显微结构对枝晶半固态衍变具有较大影响,对于原始组织粗大的树枝晶合金,即使经过长时间的保温,初生α相仍为枝晶网状结构;而原始组织细小的等轴晶迅速转变为球状结构。
3.
To observe the austenitic grain growth dynamically of T10A with different original structures during heating in vacuum.
试验结果表明 ,原始组织为片状珠光体或非平衡组织 (如下贝氏体或马氏体 )比粒状珠光体形成的奥氏体晶粒具有更强烈的长大趋势 ,前三者的急剧长大温度在 10 0 0℃左右 ,后者在 110 0℃左
2) original microstructure
原始组织
1.
With quenching and hot rolling pretreatment,25MnV steel's hardness and strength after zero time holding quenching in different original microstructures were researched by orthogonal regressive principle,and its microstructure was analyzed too.
采用正交组合回归设计试验方法,分别以淬火和热轧为预处理工艺,研究了不同原始组织条件下25MnV钢“零保温”淬火后的强度和硬度,并进行了组织分析。
3) initial parenchyma
原始薄壁组织
4) original microstructures
原始微观组织
5) initial structure
初始组织
1.
Effect of initial structure characteristic on evolution of primary phase in mold filling
初始组织特征对充型过程中初生相演变的影响
2.
The densification of initial structure was simulated by using the algorithm developed by Tikare et al.
使用的Monte Carlo法和几何模型法生成了不同颗粒形态的初始组织。
6) Primitive equation set
原始方程组