1) fluoride glass
氟化物玻璃
1.
The phase separation and crystallization of fluoride glass 8.
3ZrF4的氟化物玻璃为对象,研究了玻璃的分相和析晶。
2.
Varying contents of ZrF4 were incorporated into the fluoroaluminate base-glass having a composition of 10MgF2- 20CaF2-10SrF2-BaF2-15YF3-35AlF3(molar percent), contents of other components being adjusted properly, fluoride glasses having no visible crystallization were obtained, these glasses can reach to 8mm thick.
以10MgF_2-20CaF_2-10SrF_2-10BaF_2-15YF_3-35AlF_3(摩尔百分数)氟铝酸盐玻璃为基本组成,在玻璃中引入不同含量的ZrF_4,同时对其它组成进行适当调整,制得了厚度8mm无可见析晶的氟化物玻璃。
3.
Considering Yb3+, -Er3+ energy transfer the basis process,the up-conversion in Yb(3+)/Er(3+) doped fluoride glass is discussed,and the counter-motion has been taken into account.
讨论了掺Ｙｂ（３＋）／Ｅｒ（３＋）氟化物玻璃的上转换机制，认为Ｙｂ（３＋），－Ｅｒ（３＋）之间的能量转移上转换是主要过程，且其逆过程不可忽视。
2) fluoride glasses
氟化物玻璃
1.
The chemical stability of new oxyfluoride glasses containing telluride at different conditions was investigated.
对新型含碲氧氟化物玻璃在中性、碱性、酸性条件下的化学稳定性进行了研究。
3) fluoride glass
[化]氟化物玻璃
4) oxyfluoride glass
氟氧化物玻璃
1.
Three kinds of oxyfluoride glass were fabricated with the aim of studying the relation between Er 3+ luminescence and the fluoride micro-crystallite formed in the oxyfluoride glass.
为了研究铒离子的发光和氟氧化物玻璃中形成的氟化物微晶的关系 ,制备了三种掺铒的氟氧化物玻璃 。
2.
The slab waveguide of oxyfluoride glass was fabricated by Ag+–Na+ ion-exchange.
用Ag+–Na+离子交换法,制备了氟氧化物玻璃平面光波导。
5) non-fluoride halide glass
非氟卤化物玻璃
1.
In order to obtain applicable non-fluoride halide glasses, it is necessary to find out new glass-forming systems.
为了获得具有实用意义的非氟卤化物玻璃，有必要探索新的玻璃形成系统。
6) niobium-containing fluoride glass
铌氟化物玻璃
补充资料：氟化物玻璃
分子式：
CAS号：
性质：以氟化铍(BeF2)、氟化铅(PbF2)为主要成分的玻璃。具有低熔制温度、特低折射率、低色散、化学稳定性差，易在空气中潮解、易失透等特性。加少量偏磷酸钠可改善其化学稳定性。主要作为特种光学玻璃的基础玻璃。氟化铍与二氧化硅结构上具有相似性，常作为模拟物质，用于较低温度下研究模拟相图。