1) NiCu ferrite
镍铜铁氧体
1.
Nano-NiCu ferrite particles were manufactured by the sol-gel method.
采用溶胶 凝胶法制备了纳米镍铜铁氧体粒状材料,并对其吸波性能进行研究。
2.
The results of experiments indicate that both of these two kinds of compound ferrite have some microwave absorption property and nano-NiCu ferrite is better than nano-MnZn ferrite in the microwave absorption properties.
采用溶胶—凝胶工艺制备出纳米锰锌铁氧体和纳米镍铜铁氧体,并分别对其结构和微波波段的吸波性能进行了测试。
3) nano-size NiZnCu(Cr)-ferrite
纳米镍锌铜(铬)铁氧体
4) broad band NiCuZn series ferrite
宽频带镍铜锌系铁氧体
5) nickel ferrite
镍铁氧体
1.
Preparation and properties of the nickel ferrite/polystyrene composites
镍铁氧体/聚苯乙烯复合材料的制备与性能
2.
The results show that the precursors are directly transformed into the pure spinel nickel ferrite nano-powders at 300 ℃.
以乙酸镍、氢氧化铁和草酸为原料,用流变相反应法制备出前驱物,在不同温度下煅烧得到纳米镍铁氧体粉末。
3.
Nanocrystalline nickel ferrite was prepared by polyacrylamide gel,taking acrylamide as monomer and N,N-methylenediacrylamide as lattice agent.
通过高分子凝胶法制备了尖晶石型镍铁氧体(NiFe2O4)纳米晶。
补充资料：锂.镍矩磁铁氧体
分子式：
CAS号：
性质：以锂、镍和铁的氧化物为主要成分的一种宽温矩磁铁氧体材料。化学式(Li2O，NiO，ZnO)Fe2O3。密度4.8g/cm3。居里温度300～400％。开关速度快，开关系数(0.557～11.94)×10-6A·S/m。体积电阻率5×10-4Ω·cm。温度稳定性好。但矩形比稍低。采用电子陶瓷工艺，1000℃以上高温，在空气、氧气或氮气气氛中烧结而成。主要用作高速度、大容量电子计算机的存贮元件。是用量较大的铁氧体材料之一。
CAS号：
性质：以锂、镍和铁的氧化物为主要成分的一种宽温矩磁铁氧体材料。化学式(Li2O，NiO，ZnO)Fe2O3。密度4.8g/cm3。居里温度300～400％。开关速度快，开关系数(0.557～11.94)×10-6A·S/m。体积电阻率5×10-4Ω·cm。温度稳定性好。但矩形比稍低。采用电子陶瓷工艺，1000℃以上高温，在空气、氧气或氮气气氛中烧结而成。主要用作高速度、大容量电子计算机的存贮元件。是用量较大的铁氧体材料之一。