1) vapor of In
In气氛
1.
In order to meet the requirements of the design of radiation detectors, CdZnTe (or Cd-(1-x)Zn-xTe) wafers grown by vertical Bridgman method were annealed in the vapor of In.
为了满足辐射探测器件的需要,将生长得到的Cd_(1-x)Zn_xTe晶体在In气氛下进行退火处理能有效提高晶体的电阻率等性能。
2) atmosphere
[英]['ætməsfɪə(r)] [美]['ætmə'sfɪr]
气氛
1.
Effect of atmosphere and addition agent on the melting rate of low carbon mold powder in continuous casting;
气氛和添加剂对低碳连铸保护渣熔速的影响
2.
Study of sulfur-fixing characteristics of sulphoaluminate in different atmosphere at high temperature;
高温固硫物相硫铝酸钙在不同气氛下的固硫研究
3.
Study on SO_2 emission under various atmospheres during coal combustion;
不同气氛下燃煤SO_2的排放规律研究
3) ambience
[英]['æmbiəns] [美]['æmbɪəns]
气氛
1.
The Discussion To The Design of Indoor Ambience;
浅议室内环境设计气氛的创造
2.
Effect of heat treating ambience on luminescent properties of cerium doped silica;
热处理气氛对铈离子掺杂SiO_2发光性能的影响
3.
The paper introduce the design essentials of furnace temperature and ambience about this carbonization furnace line which is continuum-type for gases.
分析并阐述了连续式双排气体渗碳自动线炉温与气氛均匀性的设计要素。
4) atmospheres
[英]['ætməsfiə] [美]['ætməs,fɪr]
气氛
1.
Effect of Melting-Atmospheres on Irradiation-Resistance of Cerium-Doped Li_2O-Al_2O_3-SiO_2 Glasses;
熔制气氛对掺铈锂铝硅系统玻璃耐辐照性能的影响
2.
Frictional behavior of DLC films was studied in various atmospheres.
通过控制摩擦环境气氛对DLC薄膜和钢球对磨的摩擦系数进行了系统研究。
3.
The atmospheres play little part in heat decomposition of the gel before 280℃,but important role for the formation of phase in the anaphase.
气氛对于280℃前凝胶热分解过程没有影响,但在280℃后对物相形成有较大影响。
5) environment
[英][ɪn'vaɪrənmənt] [美][ɪn'vaɪrənmənt]
气氛
1.
The release of sexni- volatiles in general are con- trolled by the environment and temperature,although the release is different from element toelement.
这些实验把二氧化铀燃料碎片在空气、水蒸气和惰性气氛中加热至４６５～２０８０℃。
2.
Setting up good class environment can convey students active spirits and utilizing students subjec-tive initiative can help teachers optimize teaching.
教师在课堂上结合教学内容建立起良好的课堂情绪气氛,可以有效地使学生产生积极的情绪态度。
3.
The paper puts forward the author s elementary thinking on how to create an aesthetic environment by making use of aesthetic educating materials in history textbooks.
本文试从发掘历史教材中的美育素材 ,如何酿造美的气氛等方面提出了一些粗浅认识。
6) oxygen atmosphere
氧气气氛
1.
By using MMS-1G pin-disk high temperature & high speed friction and wear tester,the dry sliding friction and wear characteristics and wear mechanism of CrNiMo steel-H96 copper couples in oxygen atmosphere were investigated.
利用MMS-1G销盘式高温高速摩擦磨损试验机,研究了氧气气氛条件下CrN iMo钢/H96黄铜配副的干滑动摩擦磨损特性,并分析了磨损机制,结果表明:纯氧气气氛条件下,摩擦因数随着载荷和速度的增加而减小;磨损率随着载荷和速度的增加而增加。
2.
By using QG-700 pin-on-disk friction and wear tester,effects of different sliding speed and contacting pressure on the tribology properties of CrNiMo steel under high temperature and oxygen atmosphere were investigated.
以CrNiMo钢和H96黄铜组成配副,利用QG-700型高温气氛摩擦磨损试验机,研究了高温氧气气氛环境中滑动速度、接触压力等对CrNiMo钢摩擦学特性的影响。
补充资料：粉末烧结气氛
粉末烧结气氛
powder sintering atmosphere
tenmo shaoJ一eq一fen粉末烧结气氛(powde:Sintering atmo-sphere)粉末烧结时，烧结炉内的实际气氛。烧结气氛分为保护气氛、可控气氛和空气。 保护气氛用于保护烧结制品不受氧化的气氛。保护气氛分为还原性气氛和中性气氛。 还原性气氛有氢气、分解氨。(1)氢气。氢气在一定温度下具有很强的渗透性，是一种化学活性和对氧的亲和力均很强的可燃性无毒气体。氢在粉末冶金中，一方面可用作多种金属氧化物的还原剂，另一方面可用作多种粉末冶金材料和制品烧结和热处理的保护气氛。例如，钨、铝等难熔金属及硬质合金等的烧结，一般都用氢作保护气氛。尽管世界上90%以上的氢气是用夭然气和石油转化制取的，但水电解制氢技术可靠，操作维护简便。因此，粉末冶金中使用的氢气一般都是用水电解法制取的，其缺点是耗电多，成本较高。水电解制氢时，在阴极上析出氢，在阳极上析出氧。已商品化的水电解槽采用25%~30%KOH作电解液，氢气纯度高于99.7%，氧气纯度高于99.5%。(2)分解氨。分解氨是液氨经热分解所得的由氢和氮组成的混合气体，在粉末冶金中可用来作为还原剂，除某些含有与氮发生反应的成分的材料外，对其他材料的烧结也可用作保护气氛。氨在平常情况下是有刺激性臭味的无色气体。氨很容易液化，在常温加压时就可液化成液氨，液氨经气化后，在一定温度和催化剂的作用下分解而成氢与氮的混合气体，其反应式为:ZNH。一3H:+NZ。氨分解气氛的成分理论上是75环H:和25%N:。 中性气氛粉末冶金中使用的中性气氛有氮气、氨气、氦气以及真空等。可控气氛可以控制碳势或露点的气氛。可控气氛分为放热型气氛和吸热型气氛。 放热型气氛一种不需从外部供热的，由碳氢化合物气转化成的裂化气。其主要成分由co、cOZ、HZ、NZ、CH4等组成，它是一种可控气氛，但碳势较低，C02含量较高，而具有脱碳作用。根据空气与原料气不同的混合比，又有淡型和浓型气氛之分，淡型放热气氛中CO::CO=7一8.5;浓型放热气氛中CO::CO=0. 476一0. 716。淡型放热气氛的碳势很低，只能用作低碳钢、铜制品的无氧化加热气氛，而浓型放热气氛的碳势比较高一些，用作可控气氛时可以防止粉末冶金铁基、铜基零件的氧化和减少铁基零件的脱碳。放热型气氛的成分举例如下:一种原料气为甲烷的淡型放热气氛，含:10.5线COZ，1.5纬CO，1.2%HZ，余量NZ;一种原料气为甲烷的浓型放热气氛，含:5%COZ，10.5%CO，12·5%H:，0.5%CH‘，余量NZ。如果用净化方法除去其中的CO:和HZO，便可制成含CO和H:的氮基净化放热型气氛，这种净化气氛在粉末冶金中的应用可进一步扩大。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。