1) ATO nanorods
ATO纳米棒
1.
The structure and morphology of ATO nanorods were investigated by thermogravimetric analysis (TGA), transmission electron microscope (TEM), X-ray diffraction (XRD), electron diffraction (ED) and BET method.
以SnCl4·5H2O和SbCl3为原料,采用化学共沉淀法制得纳米级掺锑二氧化锡(ATO)的前驱物,经1000～1100°C焙烧1～3h,成功制备了直径为10～40nm,长为60～500nm的金红石结构的ATO纳米棒。
2.
Effects of processing parameters such as antimony content, heating temperature and heating time on the morphology and structure of ATO nanorods were investigated.
初步探讨了ATO纳米棒的形成机理,并用热重分析(TG)、透射电镜(TEM)、X-射线衍射(XRD)、比表面法(BET)对棒结构进行了表征。
3.
The structure and morphology of ATO nanorods were investigated by thermogravimetric analysis (TGA),transmission electron microscope (TEM), X-ray diffraction (XRD) and BET methods.
以SnCl_4·5H_2O和SbCl_3为原料,采用化学共沉淀法制得纳米级掺锑二氧化锡(ATO)的前驱物,在一定条件下热处理,成功制备了直径为10-30nm,长为50-500nm的金红石结构的ATO纳米棒。
2) nano ATO
纳米ATO
1.
The title contings has been developed based on aliphatic PU elastomer as binder,mixed with superdispersant and nano ATO conductive powder.
以脂肪族聚氨酯弹性树脂为基体,透明纳米ATO导电粉为导电介质,添加超分散剂,采用物理与化学相结合的分散方法对纳米ATO进行预处理。
2.
The results show that the antistatic paints will has good properties and surface resistivity of 103 Ω·cm-2 with 60%-65% of nano ATO powders, 5% of coupling agent NTC-401.
制备了一种以纳米ATO导电粉为填料,醇酸树脂为基体的复合型导电涂料,讨论了ATO的含量、偶 联剂种类、固化工艺以及溶剂对涂层导电性能的影响。
3) nano-ATO
纳米ATO
1.
Dispersibility of nano-ATO in EG for preparing antistatic PET;
纳米ATO在制备抗静电PET单体EG中的分散性
2.
Research on the antistatic property of PET fabric treated with nano-ATO
纳米ATO整理涤纶的抗静电性研究
3.
The nano-ATO/PP/PS composites were prepared by melt method.
采用熔融共混的方式制备了纳米ATO/聚丙烯/聚苯乙烯(ATO/PP/PS)纳米复合材料,分析了复合材料的微观相态结构,并对复合材料的物理力学性能及结晶与熔融行为进行了研究。
4) ATO nanopowder
ATO纳米粉
1.
TiO2 powder and ATO nanopowder were prepared respectively using the method of peptizing the amorphous Ti(OH)4 in aqueous solutions and liquid phase-hydrolysis; ATO-coated TiO2 powder was synthesized by heterogeneous nucleation method; ATO, TiOj and ATO-coated TiO2 powder coating electrode were prepared by printing method.
分别对采用回流胶溶法、液相共沉淀法制备TiO_2粉体与ATO纳米粉体；采用非均匀成核法制备ATO／TiO_2包覆粉体以及采用印刷法制备了ATO，TiO_2涂层电极和ATO／TiO_2包覆粉体多孔涂层电极进行了研究。
5) nano ATO slurry
纳米ATO浆料
6) ATO nanometer powder
ATO纳米粉末
1.
ATO nanometer powder was prepared respectively by ultrasonic hydrolysis and conventional electromagnetic agitation hydrolysis.
分别以超声水解和常规电磁搅拌水解法制备了ATO纳米粉末,对其进行了XRD,SEM,TEM检测和电阻测量,比较了两种方法制得的粉末团聚度,并从机理上作了解释。
补充资料：看纺织印染中应用纳米材料和纳米技术
纺织印染中应用纳米材料和纳米技术时，除了要解决纳米材料的制备技术之外，重要的是要解决好纳米材料的应用技术，其中关键问题是使纳米粒子和纺织印染材料的基本成分（即聚合物材料）之间处于适当的结合状态。印染中，纳米粒子在聚合物基体中的分散和纳米粒子在聚合物表面的结合是主要的应用技术问题。 制备聚合物/无机纳米复合材料的直接分散法，适用于各种形态的纳米粒子。印染中纳米粒子的使用一般采用直接分散法。但是由于纳米粒子存在很大的界面自由能，粒子极易自发团聚，利用常规的共混方法不能消除无机纳米粒子与聚合物基体之间的高界面能差。因此，要将无机纳米粒子直接分散于有机基质中制备聚合物纳米复合材料，必须通过必要的化学预分散和物理机械分散打开纳米粒子团聚体，将其均匀分散到聚合物基体材料中并与基体材料有良好的亲和性。直接分散法可通过以下途径完成分散和复合过程： 高分子溶液（或乳液）共混：首先将聚合物基体溶解于适当的溶剂中制成溶液（或乳液），然后加入无机纳米粒子，利用超声波分散或其他方法将纳米粒子均匀分散在溶液（或乳液）中。有人将环氧树脂溶于丙酮后加入经偶联剂处理过的纳米TiO2，搅拌均匀，再加入 40wt%的聚酰胺后固化制得了环氧树脂/TiO2纳米复合材料。还有人将纳米SiO2粒子用硅烷偶联剂处理后，改性不饱和聚酯。 熔融共混：将纳米无机粒子与聚合物基体在密炼机、双螺杆等混炼机械上熔融共混。如将PMMA和纳米SiO2粒子熔融共混后，双螺杆造粒制得纳米复合材料。又如利用偶联剂超声作用下处理纳米载银无机抗菌剂粒子，分散制得PP/抗菌剂、PET/抗菌剂、PA/抗菌剂等复合树脂，然后经熔融纺丝工艺加工成抗菌纤维。研究表明，将经过表面处理的纳米抗菌剂粒子通过双螺杆挤出机熔融混炼，在聚合物中可以达到纳米尺度分散，获得了具有良好综合性能的纳米抗菌纤维，对大肠杆菌、金黄色葡萄球菌的抗菌率达到95%以上（美国AATCC－100标准）。 机械共混：将偶联剂稀释后与碳纳米管混合，再与超高分子量聚乙烯（UHMWPE）混合放入三头研磨机中研磨两小时以上。将研磨混合物放入模具，热压，制得功能型纳米复合材料。 聚合法：利用纳米SiO2粒子填充（Poly（HEMA））制备了纳米复合材料。纳米SiO2粒子首先被羟乙基甲基丙烯酸（HEMA）功能化，然后与HEMA单体在悬浮体系中聚合。还有利用SiO2胶体表面带酸性，加入碱性单体4－乙烯基吡咯进行自由基聚合制得包覆型纳米复合材料。