1) acrylamide-type
丙烯酰胺型
1.
Study on Micellization Behavior of Acrylamide-type Anionic Surface Active Monomer and Copolymerization Mechanism of Surface Active Monomer and Acrylamide;
丙烯酰胺型阴离子表面活性单体的胶束化行为及其与丙烯酰胺共聚合机理
2) twin tail-type acrylamide
孪尾型丙烯酰胺
1.
A new micellar copolymerization system was constructed using sodium 2-acrylamido-dodecane sulfonate(NaAMC_12S) as a surfactant,and the copolymer of acrylamide(AM) and a twin tail-type acrylamide N,N-didodecylacrylamide(DiC_12AM) was performed.
以表面活性单体2-丙烯酰胺基十二烷磺酸钠(NaAMC12S)为表面活性剂构建了新的胶束共聚合体系,实施了丙烯酰胺(AM)与N,N-二正十二烷基丙烯酰胺(DiC12AM)的胶束共聚合,制备了含孪尾型丙烯酰胺的疏水缔合聚丙烯酰胺(HAPAM),该聚合物为三元共聚物DiC12AM/NaAMC12S/AM。
3) acrylamide
[,ækri'læmaid]
丙烯酰胺
1.
Study on the Synthesis of Cationic Polyacrylamide Via Inverse Emulsion Polymerization Method;
反相乳液聚合法合成阳离子聚丙烯酰胺的研究
2.
Study on preparation conditions of cationic polyacrylamide;
阳离子聚丙烯酰胺制备条件研究
3.
Determination of acrylamide in food by matrix solid-phase dispersion and gas chromatography-mass spectrum;
基质固相分散和气相色谱-质谱法测定食品中的丙烯酰胺
4) acryl amide
丙烯酰胺
1.
Study on the acryl amide intake in the Beijing diet;
北京地区居民丙烯酰胺膳食摄入量的研究
2.
This MW treating method was extended to treat wood flour in an acryl amide(AM)solu- tion,and FTIR showed that grafting reaction betw.
此外,用微波处理经丙烯酰胺水溶液浸润过的木粉而制备的 PVC/木粉复合材料,力学性能又得到了进一步提升;傅里叶变换红外光谱分析表明丙烯酰胺在木粉表面发生了接枝反应;扫描电镜分析也表明,经过微波接枝反应后,木粉与 PVC 的相界面连续性变好,两相相容性得到了提高。
3.
The best grafting conditions of bamboo fiber which grafted by acroleic acid(AA) and acryl amide(AM) in HNO_3 dilute solution system by planing.
用正交法探讨了竹纤维在HNO3稀溶液体系中以丙烯酸(AA)和丙烯酰胺(AM)单体接枝共聚反应的最佳条件,结果表明,当引发剂硝酸铈铵浓度为20mmol。
5) acrylic amide
丙烯酰胺
1.
Super absorbent resin of sodium polyacrylate is prepared by inverse suspension polymerization with acrylic acid and acrylic amide as the main material,span60 as dispersant,cyclohexane as the continuous phase,K2S2O8-NaHSO3 as initiator and N,N-methylene diacrylamide as cross linking agent.
采用反相悬浮聚合法,以丙烯酸和丙烯酰胺为主要原料,司班60等作为分散剂,环己烷为介质,过硫酸钾-亚硫酸氢钠为引发剂,N,N’-亚甲基双丙烯酰胺为交联剂,合成吸水树脂;考察了防粘剂、分散剂对树脂性能的影响,并对树脂的各种性能进行了分析。
2.
Cellulose in pulp is used as a raw material on which acrylic acid and acrylic amide are grafted when superabsorbent is polymerized.
采用纸浆纤维素为分子骨架,接枝丙烯酸及丙烯酰胺制备高吸水树脂。
3.
AA-AM supper absorbent resin was synthesized from acrylic acid(AA) and acrylic amide(AM) by inverse suspension method.
对反相悬浮法制备丙烯酸 (AA)和丙烯酰胺 (AM)二元共聚高吸水性树脂的工艺进行了研究。
6) acrylamide(AM)
丙烯酰胺
1.
P(DMDAAC-AM)(PDA) was prepared from dimethyldiallyammonium chloride(DMDAAC) and acrylamide(AM) by inverse emulsion polymerization with water-soluble redox initiator.
用水溶性的氧化还原引发剂引发,通过反相乳液聚合制备了二甲基二烯丙基氯化铵(DMDAAC)-丙烯酰胺(AM)共聚物(PDA),聚合反应中水/油体积比为1。
2.
Technology of gelcasting for insulator body was studied using acrylamide(AM)as catalyst and ceric ammonium nitrate as initiator,N,N,N',N'tetramethylethylenedimaine as catalyst,N,N'methylenenebisacrylamide(MBAM)as cross linker.
以丙烯酰胺为单体,硝酸铈铵为引发剂,N,N,N',N'-四甲基乙二胺为催化剂、N,N'-亚甲基双丙烯酰胺为交联剂,研究了电瓷坯体的凝胶注模成型工艺,并探讨了不同工艺条件对料浆原位凝固成型的影响规律以及成型的电瓷坯体的烧成性能和显微结构。
3.
In this paper, the acrylamide(AM) was polymerized, then we can got the amphoteric polymer-acrylamide through Hofmann degradation.
丙烯酰胺单体通过均聚合成和霍夫曼降解得到丙烯酰胺两性聚合物,填加适量NN-亚甲基丙烯酰胺与减水剂复配应用在混凝土中,提高混凝土的工作性能、力学性能和耐久性能。
补充资料：N-(羟甲基)-2-丙烯酰胺与2-丙烯酰胺的聚合物
CAS：26338-66-9
分子式：(C3H5NO·C4H7NO2)x
中文名称：N-(羟甲基)-2-丙烯酰胺与2-丙烯酰胺的聚合物
英文名称：2-Propenamide, N-(hydroxymethyl)-, polymer with 2-propenamide 2-Propenamide,N-(hydroxymethyl)-,polymer with 2-propenamide
分子式：(C3H5NO·C4H7NO2)x
中文名称：N-(羟甲基)-2-丙烯酰胺与2-丙烯酰胺的聚合物
英文名称：2-Propenamide, N-(hydroxymethyl)-, polymer with 2-propenamide 2-Propenamide,N-(hydroxymethyl)-,polymer with 2-propenamide
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条