1) effective titanium
有效钛
1.
08%; the increase in strength is dependent on the content of effective titanium that is rela.
08%时,高强耐候钢的晶粒尺寸随着钛含量的增加基本不变;高强耐候钢强度的提高主要取决于钢中有效钛的含量,有效钛不仅与钛的含量有关,而且还与S,N的含量有关;在有效钛含量一定的条件下,析出强化的大小主要取决于轧后的卷取温度。
2.
The results show that effective titanium content ω(Ti)e is the main parameter for controlling the austenite gain size and the grain coarsening temperature of the steel.
结果表明,有效钛含量W(Ti)_e是决定试验用钢奥氏体晶粒度及晶粒粗化温度的主要参数。
3.
The results show that effective titanium ( Ti e ) content is the main parameter for controlling the austenite grain size and the grain coarsening temperature of the steel.
结果表明，有效钛（ Ｔｉｅ）是决定２０ Ｍｎ Ｍｏ Ｂ钢奥氏体晶粒度和晶粒粗化温度的主要参数。
2) effective titanium content
有效钛含量
1.
The influences of six kinds of conditioning heat treatments and different effective titanium contents on the behavior of austenite grain coarsening were studied.
研究了6种预先热处理工艺及有效钛含量对18CrMmVB钢奥氏体晶粒长大行为的影响。
4) organotitanium compounds
钛有机物
5) organic titanium
有机钛
1.
A series of chitosan(CTS) hydrogels crosslinked by organic titanium(OT) were prepared.
以有机钛(OT)为交联剂,制备了一系列壳聚糖(CTS)基复合凝胶,用动态粘弹仪对不同配比的复合凝胶进行了流变性能的测试,以储能模量G′和损耗模量G″为参数,研究了凝胶过程中复合凝胶的动态粘弹行为,并运用Winter-Chambon理论准确界定了不同浓度体系溶胶-凝胶转变点。
6) titanyl organic compound
钛氧有机物
1.
The solid product titanyl organic compound mixture comprised of TiO(OOCCH 3) 2 and TiO(OC 4H 9)(OOCCH 3) was obtained.
将 2 0ml钛酸丁酯及 30ml乙酐在密闭容器中与 5 0ml环己烷混合 ,在 70～ 85℃反应 30min ,生成微细的非晶钛氧有机物 ;经FT IR和TGA分析 ,该物质被确认为计量式是TiO(OOCCH3 ) 2 和TiO(OC4 H9) (OOCCH3 )的混合体 。
补充资料：5t钛还原蒸馏炉(遵义钛厂)
5t钛还原蒸馏炉(遵义钛厂)
5t钛还原蒸馏联合炉(遵义钛厂)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条