1) carbothermal reduction nitridation method
碳热-氮化法
2) carbothermal reduction and nitridation
碳热还原氮化法
1.
One way is the hot-pressing process using chemical starting materials, and another is Carbothermal Reduction and Nitridation process using natural starting materials.
目前,制取Sialon耐火材料的途径通常有两种:(一)利用化学原料氮化法合成;(二)利用天然原料碳热还原氮化法合成。
3) carbothermal reduction nitridation
碳热还原氮化法
1.
The(Ca,Mg) α′-Sialon/BN composite powder was synthesized by carbothermal reduction nitridation with boron-rich slag as main starting material,of which the composition is(Ca,Mg)xSi12-3xAl3xOxN16-x where x is ranging from 0.
以富硼渣为主要原料,采用碳热还原氮化法合成了组分为(Ca,Mg)xSi12-3xAl3xOxN16-x(x=0。
4) carbothermal nitridation
碳热氮化
1.
Preparation of SiC-AIN composite ultrafine powder by sol-gel and carbothermal nitridation is reported in this paper.
用溶胶－凝胶碳热氮化法在１５５０～１６５０℃，５０ｍｉｎ下制得平均粒径为０。
5) thermal nitridation
热氮化法
1.
SiO_xN_y ultra thin films were grown by thermal nitridation with NiO and NH_3 used as the react gas respectively.
利用α—台阶仪测量了SiO_xN_y薄膜的厚度,实验研究了Si衬底晶向、氮化温度、生长时间和氮化气氛对SiO_xN_y薄膜厚度的影响,定性地讨论了热氮化法制备SiO_xN_y薄膜的生长机制。
补充资料：碳热还原法
在高温下用碳还原金属氧化物制取金属的方法。例如，在高温下用碳还原氧化亚铁可得金属铁：
FeO+C─→Fe+CO其热力学依据是：金属氧化物的生成自由能变化ΔG(MO)是随温度的升高而逐渐增高（负值变小），而一氧化碳的生成自由能变化ΔG(CO)却是随温度的升高而明显降低（负值变大）,所以当温度升高到ΔG(CO)-ΔG(MO)＜0时，原来在低温下不能进行的反应变得能够进行。这种方法的优点是焦炭价廉易得，缺点是必须使用鼓风炉或电熔炉，而且许多金属会生成碳化物。
FeO+C─→Fe+CO其热力学依据是：金属氧化物的生成自由能变化ΔG(MO)是随温度的升高而逐渐增高（负值变小），而一氧化碳的生成自由能变化ΔG(CO)却是随温度的升高而明显降低（负值变大）,所以当温度升高到ΔG(CO)-ΔG(MO)＜0时，原来在低温下不能进行的反应变得能够进行。这种方法的优点是焦炭价廉易得，缺点是必须使用鼓风炉或电熔炉，而且许多金属会生成碳化物。