1) SiC/Si_3N_4 nano powder
SiC/Si3N4复合纳米粉
2) Si 3N 4/SiC nanocomposite
Si3N4/SiC纳米复合材料
1.
In this paper,the basic preparing process and mechanical properties for Si 3N 4/SiC nanocomposites are reviewed,the main reasons of the improvements in these properties are analyzed,and the mechanism of strengthening and toughening in this material are discussed.
本文评述了Si3N4/SiC纳米复合材料的制备工艺及其力学性能 ,分析了力学性能提高的主要原因 ,讨论了材料中存在的强化增韧机
3) SiC/Fe_3O_4 composite nanopowders
纳米SiC/Fe_3O_4复合粉体
4) silicon nitride nanoparticles(Si3N4)
纳米Si3N4粉体
1.
Low-molecular-mass CSM was prepared by degrading CSM,and it was used to modify silicon nitride nanoparticles(Si3N4).
用降解氯磺化聚乙烯橡胶(CSM)的方法制备了低分子量氯磺化聚乙烯(LMCSM),将其作大分子表面改性剂对纳米氮化硅(Si3N4)粉体进行表面修饰,对改性前后的纳米Si3N4粉体采用沉降实验、FT-IR、TEM、TGA等方法进行了表征。
5) SiC nanometer powder
SiC纳米粉
1.
The results show that oxygen mainly exists in the form of physical adsorption for fresh SiC nanometer powder(adsorbed oxygen-78.
借助于TEM、IR和XPS分析；对新鲜的SiC纳米粉表面和不同存放时间及处理条件下的样品表面进行分析比较，发现新鲜的作品表面主要以物理吸附氧为主（78。