1) body galvanized steel sheet
车身镀锌钢板
1.
Performance prediction in spot welding of body galvanized steel sheets based on artificial neural network and its optimization;
亦即该优化神经网络模型可有效地实现对车身镀锌钢板点焊性能的预测,且预测精度和准确率较高,符合工程需要,具有一定的实用价值。
2) automobile sheets
汽车车身用镀锌板
3) galvanized sheet steel
镀锌钢板
1.
The commercial hot-dip galvanized sheet steel was investigated for its corrosion behavior in three different seawater zones in Qingdao with electrochemical measurement,weight loss test and SEM.
开展了热镀锌钢板在青岛不同海水区带的实海腐蚀测试,并利用电化学测试、失重腐蚀测试和扫描电镜研究了镀层的海水腐蚀行为。
2.
With the rapid development of Chinese economy, demands for galvanized sheet steels increased significantly because of the rapid development of construction and automotive industry during the last decade.
随着国内经济的持续稳定发展,在过去的10年中,由于建筑和汽车行业的快速发展,对镀锌钢板的需求持续旺盛。
3.
occured in forming and after coating of the prephosphating galvanized sheet steel,this paper demonstrates analyses on all kinds of influential factors happened in production and forming in detail,after that,provides some solutions on purpose.
为解决预磷化镀锌钢板加工成形、涂装后易出现的条影、针孔、粗糙等问题,对其生产及加工成形过程中的各种影响因素进行了详细分析,并有针对性地提出一般的解决办法。
4) zinc coated steel
镀锌钢板
1.
Effect of TiC coating on electrode tip surface on electrode degradation during resistance spot welding zinc coated steel;
点焊镀锌钢板时电极表面熔敷TiC涂层对电极失效的影响
2.
Effect of zinc coating on arc heating behavior for joining Al and zinc coated steel by welding-brazing process
镀锌层对铝/镀锌钢板CMT熔-钎焊电弧加热行为的影响
3.
The effect of TiC coating in electrode tip surface on spheriform electrode degradation during resistance spot welding zinc coated steel was investigated by SEM,EDX and XRD.
利用SEM、EDX和XRD等方法分析了在点焊镀锌钢板时球形电极表面熔敷TiC涂层对电极失效的影响。
5) galvanized steel
镀锌钢板
1.
Study on the effects of components in phosphating solution on properties of phosphating film of galvanized steel;
镀锌钢板磷化液组分对磷化膜性能的影响
2.
The film forming mechanism of a novel calcium modified phosphating solution on galvanized steel was studied.
研究了一种新型的钙改性磷化液在镀锌钢板上的成膜机理。
3.
A Phosphating process for galvanized steel plate was developed.
研究出一种应用于镀锌钢板的磷化工艺,对磷化液中各组分的作用进行了分析、讨论,尤其氯离子对磷化膜性能的影响。
6) zinc coated steels
镀锌钢板
1.
5wt% has been studied during spot welding of zinc coated steels .
5 %的铜基复合材料 (Ti B2 /Cu)作电极在点焊镀锌钢板时的失效形式 ,结果表明 :Ti B2 /Cu电极在点焊镀锌钢板时的平均使用寿命是 Cu Cr Zr合金电极的 4倍 ,Ti B2 /Cu电极的失效形式主要是表面的合金化 ,少量的细碎翻边、粘附和坑蚀 ,不出现蘑菇状 ,是一种较好的点焊电极材
2.
A series of spot welding technology and joint tensile shear tests for uncoated low carbon, electroplated and two kinds of hot dipped zinc coated steels were made to improve the quality of spot welding joint for zinc coated steels.
为提高镀锌钢板点焊接头的质量，对普通冷轧钢板、电镀锌钢板和两种镀锌层厚度不同的热镀锌钢板进行了一组点焊工艺及接点强度试验，并对试验结果进行了计算机回归分析，分别得出了这几种材料在不同的焊接电流、焊接时间下的点焊熔核直径或接头拉剪强度变化曲线以及点焊飞溅临界曲线。
补充资料：镀锌钢板生产
镀锌钢板生产
production of zinc-coated steel sheet
2少，，:入，，。 r凸、!It一哪1一”1，8李攀， 久4L二习12 图1改良森吉米尔法带钢连续热镀锌工艺流程 l一开卷;2一切头;3一焊接;4一活套;5一无氧化加热;6一还原; 7一冷却;8一镀锌;9一矫直;10一飞剪;一卷取;12一垛板成海绵状铁，最后带钢在保护气氛中冷却到稍高于锌废保护气体在无氧化加热炉内然烧可节约一部分燃液温度下进入锌锅镀锌.料，省掉了还原炉前的密封辊构件。 改良森吉米尔法是从老法发展和改进形成的。20世纪80年代中国在上海建成的现代化热镀锌该法的核心是带钢先进行无氧化加热，去除表面油脂、机组的工艺流程如图2所示。该机组的特点是:卧式的灰尘和水分，然后进入充有含氢15%~30%和氮85%氧化还原炉为大大缩短机组长度的立式炉所取代，(见一7。%的保护气体的还原炉内完成常化或再结晶退火彩图插页第14页)带钢表面清洁，板形好有利于镀层并还原表面的氧化铁。改良森吉米尔法镀锌的工艺流厚度控制，采用电感应加热陶瓷锌锅，锌液成分均匀，程如图1所示。老法的氧化和还原是分别进行的，而新不产生底渣，锌锅寿命长，装有防颤辊用来保持带钢运法则将无氧化快速加热炉同还原炉用通道连接，带钢行稳定;二辊光整机和拉伸弯曲矫直机均配有换辊装从无氧化加热炉内通过时几乎不发生氧化。新法同老置，可在不中断带钢运行的情况下同时更换上下辊，设法相比:可提高机组产量;降低了保护气氛中氢的浓有在线镀层测厚仪，可自动控制镀层重量，全线操作由度，从而减少了成本和氢爆炸的危险性;还原炉排出的计算机控制。 一毕一尸-」-一一一红一华一一一三一一，一一工-一 零护寻彝巍鲡 图2带钢热镀锌工艺流程 1一开卷和焊接.2、5一活套.3一退火和热锭锌，4一冷却和纯化，6一光整和拉娇.7一卷取 电被锌工艺电镀锌是将带钢作为阳极，从含有锌盐溶液的电镀槽中通过，在直流电作用下表面获得门厂1，，l}/‘锌被层。(见彩图插页第15页)电镀锌分单面镀锌和双一十n日汀护尸L竹Z卜边面镀锌两种。电镀锌按被液性质、镀槽形式和阳极性质{11111流「}vL【’.)」‘分类。镀液有碱性和酸性之分。由于碱性电解液稳定性2邓脚_111、T娜差，镀层不均匀，多被酸性取代。酸性电解液的成分是水刀、‘毛己znso·’zncl，NaZ’zn(cN)‘。镀槽形式有立式、径向。「，’‘吕‘~4‘.‘叼.2‘、“乙~吞‘、~‘’产毛。~，目产护~’刁一一，、~’切“b式和卧式3种(见图3)。由于前两种分别只适用于双面镀和单面镀，现今多采用槽体水平的卧式电镀槽，且尸‘1久!’‘}双面镀和单面镀都可完成。