1) high temperature in-situ X-ray diffraction
高温原位X射线衍射
1.
The microstructures and properties of 7A52 aluminum alloy under different homogenization conditions were studied by hardness test,electrical-conductivity measurement,optical metallography and high temperature in-situ X-ray diffraction.
采用硬度、电导率测量、金相和高温原位X射线衍射分析技术研究不同均匀化处理条件下7A52铝合金组织与性能的变化规律,着重讨论不同均匀化处理条件下合金的物相组成及其演变、基体固溶体固溶度的变化与合金硬度和电导率的关系。
2) high pressure in situ X-ray diffraction
高压原位X射线衍射
3) high temperature X-ray diffraction
高温X射线衍射
1.
The phase transformation of thermal explosion synthesized Al-Ti-C at different temperature is investigated with high temperature X-ray diffraction,and the transformation features of the Al-Ti-C microstructure are discussed by morphological analysis of synthesized product by using SEM.
采用高温X射线衍射原位观察Al-Ti-C热爆合成产物的物相变化,通过扫描电镜(SEM)分析合成产物的组织形貌,探讨热爆合成Al-Ti-C组织转变规律。
4) In situ XRD
原位X射线衍射
1.
The intercalation process of high temperature(2 250℃)treated petroleum coke in the electrolytes 1mol/L LiClO 4+EC/DEC(1∶1)and 1mol/L LiClO 4+PC/DME(1∶1)were investigated by in situ XRD.
采用原位X射线衍射技术 ,研究了经 2 2 5 0℃高温热处理的石油焦在 1mol/LLiClO4 +EC/DEC( 1∶1)和在 1mol/LLiClO4 +PC/DME( 1∶1)两种电解液中的嵌锂过程 ,结果表明 :在 1mol/LLiClO4 +EC/DEC( 1∶1)电解液中的嵌入物为锂离子 ,在 1mol/LLiClO4 +PC/DME( 1∶1)电解液中的嵌入物主要为溶剂化锂离子。
5) in-situ X-ray diffraction
原位X-射线衍射
6) in situ X-ray diffraction
原位X射线衍射
1.
The dispersion of VO_x and MoO_x on Al_2O_3 was investigated by means of in situ X-ray diffraction.
采用原位X射线衍射技术考察了机械研磨法和浸渍法制备的负载型VOx(MoOx)/Al2O3催化剂在空气中升温时的晶相变化。
2.
Sodium salt-modified Mn/SiO_2 catalysts have been characterized by in situ X-ray diffraction.
采用原位X射线衍射法对高温下不同钠盐修饰的Mn/SiO2催化剂物相结构进行了研究。
3.
Both in-diffusion in O 2 and out-diffusion in N 2 of oxygen at 325℃ in c-axis-oriented YBa 2Cu 3O 6+x film,deposited on single-crystal (100) SrTiO 3 by direct current sputtering,were studied by in situ X-ray diffraction on a Rigaku D/Max-RB diffractometer.
用原位X射线衍射法研究了磁控溅射c取向YBa2 Cu3 O6+x/SrTiO3 (YBCO/STO)优质超导外延膜在 3 2 5℃氧气中的进氧过程和氮气中的脱氧过程。
补充资料：X射线粉末衍射法
分子式：
CAS号：
性质：在X射线衍射分析中，采用单色X射线和粉末状多晶样品进行衍射的一种方法。多晶试样大多数情况是多晶粉末，也可以是多晶片或丝。衍射线条的位置、强度，可用德拜法、聚焦法或针孔法等照相记录。粉末法主要用于物质鉴定、晶体点阵常数、多晶体的结构、晶粒大小、高聚物结晶度测定等。
CAS号：
性质：在X射线衍射分析中，采用单色X射线和粉末状多晶样品进行衍射的一种方法。多晶试样大多数情况是多晶粉末，也可以是多晶片或丝。衍射线条的位置、强度，可用德拜法、聚焦法或针孔法等照相记录。粉末法主要用于物质鉴定、晶体点阵常数、多晶体的结构、晶粒大小、高聚物结晶度测定等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条