1) valid shaping
有效成形
2) the effective heat of formation
有效形成热
1.
Based on Miedema semi-empirical model and an empirical specific heat equation, the effective heat of formation and its temperature dependence were calculated for Fe-Sn and Ni-Sn systems.
以Miedema半经验模型和比热容随温度有效形成热变化的经验公式为基础,结合基本热力学关系式对Fe-Sn和Ni-Sn体系的有效形成热及有效形成热随温度的变化进行了计算。
3) effective heat of formation model
有效形成热模型
1.
Because metal ion implantation into metal at elevated temperature possessed the characteristics of non-equilibrium interface reaction, the effective heat of formation model was built to predict intermetallics formation during metal ion implantation.
鉴于金属离子高温注入金属具有非平衡界面反应特性,预测金属离子高温注入金属合成金属间化合物的有效形成热模型中,有效形成热通过形成金属间化合物的形成热,以及二元合金系的有效浓度中控制元素的浓度和形成金属间化合物的控制元素浓度的比值之积计算。
4) the formation of valid capital
有效资本形成
5) Effective Capital Formation
资本有效形成
6) forming-process of effective charge carriers
有效载流子形成过程
1.
A forming-process of effective charge carriers is found before steady light-emmitting.
着重指出在稳定发光之前有一个有效载流子形成过程。
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。