1) zinc selenium polycrystal
ZnSe多晶
2) ZnSe single crystal
ZnSe单晶
1.
A ZnSe single crystal with diameter of 25mm and length of 3mm was grown at a correct temperature and with I_2.
采用化学气相输运法(CVT)在适合的温度和I2含量的条件下,生长出了25mm×3mm的ZnSe单晶,位错密度为6。
2.
High quality ZnSe single crystals were grown by high-pressure Bridgman method(HPB)at 1530℃ under argon gas atmosphere.
采用物理气相输运法对ZnSe(4N)多晶原料在850℃±10℃进行提纯,再用高压坩埚下降法在1530℃、氩气保护气氛下生长出高质量ZnSe单晶体。
3) ZnSe crystal
ZnSe晶体
1.
Preparation of ZnSe crystal from pure Zn and Se;
ZnSe晶体制备的工艺研究
2.
ZnSe crystal was synthesized.
制备了ZnSe晶体 ,对其生长和加工工艺进行了研究 ,提出了一些合理的解决办法。
3.
ZnSe crystals with different morphologies were grown using the as-prepared ZnSe nanopowder by changing reaction time.
用X射线衍射(XRD)、透射电子显微镜(TEM)和扫描电子显微镜(SEM)等技术手段,分别对产物进行了表征,并从ZnSe晶体的结构上对其形貌的形成进行了初步分析。
4) ZnSe bulk single crystals
ZnSe体单晶
6) ZnSe single crystals
ZnSe单晶
1.
ZnSe single crystals were grown by the chemical vapor transport(CVT) method in one step,using Zn and Se elements as the raw materials and the iodine as the transport agent.
本文直接以高纯Zn、Se单质为原料,加入少量碘单质作为反应输运剂,用化学气相输运(CVT)的方法一步成功的生长出了ZnSe单晶。
补充资料：多晶莫来石晶须(纤维)
分子式：
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。