1) ZnO process
氧化锌法
2) zinc oxide by zinc hydrometallurgy
湿法氧化锌
3) Zinc membrane oxidation
锌膜氧化法
4) indirect zinc oxide
间接法氧化锌
1.
on its particle surface during vulcanization;the modulus at 300% and abrasion resistance of vulcanizate increased,and the compression set and compression fatigue temperature-rise decreased by using nano-zinc oxide instead of conventional indirect zinc oxide in equal weigh.
以纳米氧化锌等量替代普通间接法氧化锌 ,可提高硫化胶的 3 0 0 %定伸应力和耐磨性 ,减小压缩永久变形 ,降低压缩疲劳温升 ;以纳米氧化锌减量 5 0 %替代间接法氧化锌 ,仍可保证硫化胶的性能要求。
2.
The results showed that the Mooney viscosity of compound decreased,the Mooney scorch time extended and the curing behavior changed little by using nano-zinc oxide in reduced weight instead of indirect zinc oxide;the tear strength,abrasion resistance and H pull-out of vulcanizate increased;the endurance and average tread wear of test tire improved;and the cost of compound dereased.
用纳米氧化锌减量替代间接法氧化锌 ,胶料的门尼粘度下降 ,门尼焦烧时间延长 ,硫化特性基本保持不变 ;硫化胶的撕裂强度、耐磨性及H抽出力有所提高 ;试验轮胎的耐久性能及累计平均磨耗里程均较生产轮胎有所提高 ;可适当降低胶料成本。
5) zinc oxide desulfurization
氧化锌法脱硫
补充资料：直接法氧化锌
分子式：
CAS号：
性质：以锌矿石为原料制备的氧化锌，直接法氧化锌是用锌矿粉与无烟煤、石灰按比例混合成球，经还原冶炼制得锌蒸气，再用空气氧化而成。其氧化锌含量约98.0％，低于间接法氧化锌，根据锌矿石种类的不同，直接法氧化锌可以含有氧化铅、氧化铁、二氧化硫、三氧化硫、氯等。
CAS号：
性质：以锌矿石为原料制备的氧化锌，直接法氧化锌是用锌矿粉与无烟煤、石灰按比例混合成球，经还原冶炼制得锌蒸气，再用空气氧化而成。其氧化锌含量约98.0％，低于间接法氧化锌，根据锌矿石种类的不同，直接法氧化锌可以含有氧化铅、氧化铁、二氧化硫、三氧化硫、氯等。