1) ultrafine flake alumina
片状超细α-Al2O3
2) plate-like
片状
1.
The effects of plate-like alumina seed amount on the microstructure and properties of alumina ceramics prepared by pressureless sintering were studied,when plate-like alumina single crystal particles were used as seeds and CaO-Al2O3-SiO2(CAS) were used as additives.
以片状氧化铝单晶颗粒为晶种,CaO-Al2O3-SiO2(CAS)为添加剂,采用无压烧结研究了晶种加入量对氧化铝陶瓷显微结构与性能的影响。
2.
A process for the preparation of different particles of CaC03 is intruducted, the effect of various factors on CaCO3 crystal is discussed and spherical and plate-like calcium carbonate with small partical size are obstained.
采用溶液法制备了不同晶形碳酸钙,讨论了各种因素对碳酸钙结晶的影响,并得到了粒径较小的球状和片状碳酸钙。
3.
The effects of plate-like alumina seed additions on the microstructure and properties of alumina ceramics were studied, when plate-like alumina single crystal particles were used as seeds and CaO-Al2O3-SiO2(CAS) were used as additives.
本文以片状氧化铝单晶颗粒为晶种,CaO-Al2O3-SiO2(CAS)为添加剂,研究了晶种加入对氧化铝陶瓷显微结构与性能的影响。
3) Flake
片状
1.
The ultrafine flake copper particles with diameter from 1 μm to 10μm were prepared by using chemical reduction method with ascorbic acid as reducing agent.
采用液相化学还原法,以抗坏血酸为还原剂,NH3·H2O、乙二胺或EDTA为络合剂,制备了1～10μm表面光滑的片状超细铜粉。
4) platelike
片状
1.
Preparation of platelike CaCO_3 by emulsion method;
乳液法制备片状CaCO_3
2.
The influence factors on the formation of platelike crystalline α-Al2O3 powders were investigated by XRD and SEM.
本研究以工业氢氧化铝粉体为原料,加入矿化剂和晶种, 通过高温固相反应制备出分敌均匀的片状α-Al2O3粉体。
5) flake-like
片状
1.
Based on the principles of biomineralization,nano flake-like hydroxyapatite(HA) were synthesized through biomimetic method using Ca(NO3)2·4H2O and(NH4)3PO4·3H2O as reagents and chondroitin sulfate as template.
依据生物矿化的原理,以硫酸软骨素(ChS)为模板合成了片状纳米羟基磷灰石(HA)。
6) sheet-like morphology
片状形貌
参考词条
补充资料：染料细粉及超细粉
分子式：
CAS号：
性质：非水溶性染料或不易溶染料常采用的剂型。如分散染料、还原染料等对粒度及粒度分布均有一定要求，要求相对集中，过细、过粗，均对使用有不良影响。染料生产企业对本企业的产品均作了规定。这些染料产品一般多在2μm到上到4μm范围内，如对某些分散染料要求控制在1μm左右，分散性能4～5级，还原染料也与分散染料近似，故有超细粉之称。为使染料产品达到上述细度，常采用万能粉碎机或砂磨、球磨等进行粉碎。
CAS号：
性质：非水溶性染料或不易溶染料常采用的剂型。如分散染料、还原染料等对粒度及粒度分布均有一定要求，要求相对集中，过细、过粗，均对使用有不良影响。染料生产企业对本企业的产品均作了规定。这些染料产品一般多在2μm到上到4μm范围内，如对某些分散染料要求控制在1μm左右，分散性能4～5级，还原染料也与分散染料近似，故有超细粉之称。为使染料产品达到上述细度，常采用万能粉碎机或砂磨、球磨等进行粉碎。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。