1) Melt intercalation
熔融插层法
1.
Polypropylene(PP)/Montmorillonite(MMT) nanocomposites were prepared by melt intercalation method using a twin-screw extruder.
采用熔融插层法在双螺杆挤出机中制备了聚丙烯(PP)/蒙脱土(MMT)纳米复合材料,纳米复合材料机械性能测试结果表明,当有机MMT质量分数为2%时,复合材料的弯曲强度明显优于PP。
2.
Polyethylene(PE)/montmorillonite(MMT)nanocomposites were prepared through melt intercalation using maleic anhydride modified PE (PE-g-MAH) as a compatibilizer.
通过加入适量马来酸酐接枝聚乙烯(PE-g-MAH),用熔融插层法制备了聚乙烯(PE)／蒙脱土(MMT)纳米复合材料,采用X射线衍射(XRD)、透射电镜(TEM)等表征了复合材料的微观结构和形态。
3.
Polyethylene/Polyethylene modified with maleic anhydride /Montmorillonite (PE/ PEMA//MMT) nano - composites are synthesized by melt intercalation.
采用熔融插层法制备了聚乙烯/马来酸酐接枝聚乙烯/蒙脱土(PE/PEMA/MMT)纳米复合材料,研究了不同质量分数的蒙脱土对聚乙烯力学性能、热稳定性能及对有机溶剂的阻隔性的影响,并用X射线衍射法对材料的微观结构进行了表征。
2) melting intercalation
熔融插层法
1.
PP/MMT nano-composites were prepared by melting intercalation method.
通过熔融插层法制备了聚丙烯/蒙脱土(MMT)纳米复合材料,讨论了不同表面处理剂处理有机MMT以及MMT的填充量对复合材料的力学性能、热性能的影响,通过透射电镜(TEM)、X射线衍射、偏光显微镜等进一步研究了复合材料的微观结构。
2.
It is mainly introduced how to prepare the composite system of epoxy resin/MMT by melting intercalation, and apply to annular-oxygen and rich zinc antiseptic dope.
利用熔融插层法制备环氧树脂/蒙脱土复合体系,并将其应用于环氧富锌防腐涂料中。
3) melting replacement intercalation method
熔融置换插层法
1.
The kaolinite/benzamide intercalation compound was prepared by the melting replacement intercalation method with hard kaolinite from Pingxiang city as materials and the kaolinite/dimethyl sulphoxide as intercalation precursor.
采用萍乡硬质高岭土为原料,以高岭石/二甲基亚砜为前驱体,采用熔融置换插层法成功制备出高岭石/苯甲酰胺插层复合物,对高岭石/苯甲酰胺插层复合物采用X射线衍射、红外光谱、热重-差热分析、扫描电镜进行了表征。
4) melt intercalation
熔融插层
1.
Preparation of HDPE/MMT composite with melt intercalation method;
熔融插层法制备HDPE/MMT共混物
2.
Preparation of polypropylene / montmorillonite nanocomposites by melt intercalation;
熔融插层法制备聚丙烯/蒙脱土纳米复合材料
3.
Progress in melt intercalation preparation of polymer-layered silicates nanocomposites;
熔融插层制备聚合物层状硅酸盐纳米复合材料研究进展
5) melt-intercalation
熔融插层
1.
The HDPE/LDH nanocomposites were synthesized with the melt-intercalation method.
采用熔融插层法制备了高密度聚乙烯(HDPE)/层状双氢氧化物(LDH)纳米复合材料。
2.
Nylon 66/montmorillonite nanocomposites were prepared by melt-intercalation process using the twin-screw extruder.
采用熔融插层法通过双螺杆挤出机制备了PA66/蒙脱土(MMT)纳米复合材料,其综合力学性能较纯PA有显著的提高。
6) Melting intercalation
熔融插层
1.
Study of Property of PP/Montmorillonite Composite by Melting Intercalation;
熔融插层PP／蒙脱土复合材料性能的研究
2.
Advance in Research on Nano-meter Composite by Melting Intercalation;
熔融插层法制备聚合物复合材料的研究进展
3.
The title coatings has been prepared by use of melting intercalation technology to introduce the OMMT into epoxy resin system.
利用熔融插层法将有机蒙脱土引入环氧树脂体系,制备出含有纳米分散蒙脱土的无溶剂环氧涂料。
补充资料：为再结合熔融石英制品、熔融石英陶瓷制品
分子式：
CAS号：
性质：又称为再结合熔融石英制品、熔融石英陶瓷制品或石英玻璃烧结制品。具有良好的化学稳定性。抗酸性和抗冲刷性强。高温机械强度大。热膨胀系数低。气孔率低。导电率低。但在1100℃以上长期使用时，制品中的石英会向方石英转变，使制品产生裂纹和剥落。以熔融石英为原料，经粉碎、成型、干燥、烧成而制得。制法有泥浆浇注法、蜡注法、捣打法、半干压法和等静压成型等。由于在烧成时收缩小，可以制得尺寸精确的制品。可用于制作耐酸容器、反应罐内衬耐酸部件等。冶金工业中用其制成浸入式水口，使用效果很好。
CAS号：
性质：又称为再结合熔融石英制品、熔融石英陶瓷制品或石英玻璃烧结制品。具有良好的化学稳定性。抗酸性和抗冲刷性强。高温机械强度大。热膨胀系数低。气孔率低。导电率低。但在1100℃以上长期使用时，制品中的石英会向方石英转变，使制品产生裂纹和剥落。以熔融石英为原料，经粉碎、成型、干燥、烧成而制得。制法有泥浆浇注法、蜡注法、捣打法、半干压法和等静压成型等。由于在烧成时收缩小，可以制得尺寸精确的制品。可用于制作耐酸容器、反应罐内衬耐酸部件等。冶金工业中用其制成浸入式水口，使用效果很好。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条